Thermal Shock Behavior of a Novel TiCx–Ni3(Al,Ti)/Ni Functionally Graded Composite
Qun Yu,Zhenying Huang,Guangming Zheng,Wenqiang Hu,Cong Lei,Yuanbo Wang,Yidan Jiao,Hongxiang Zhai
DOI: https://doi.org/10.1007/s12540-020-00836-0
IF: 3.451
2020-08-13
Metals and Materials International
Abstract:<span class="a-plus-plus abstract-section id-a-sec1"><p class="a-plus-plus">This paper focuses on the study of thermal shock behaviors of a novel TiC<sub class="a-plus-plus">x</sub>–Ni<sub class="a-plus-plus">3</sub>(Al,Ti)/Ni functionally graded material (FGM) fabricated from Ti<sub class="a-plus-plus">3</sub>AlC<sub class="a-plus-plus">2</sub> and Ni powders. Thermal shock resistance of resulted FGM was conducted by water quenching at different temperatures, mechanical properties and microstructures after thermal shocks were correspondingly determined and characterized. The microstructure of the FGM after thermal shocks shows no cracks of instability failure between the transition zones, and the reinforcement phases were closely combined with the matrix. Meanwhile, compared with the strength of 1329 MPa without thermal shock, when the temperature of the thermal shock reached 800 °C and 1000 °C respectively, with 10 repeated heat-water quench cycles, the residual flexural strength of FGM decreased slightly, but it could still reach 1100 MPa. Notably, the strength can still maintain at 843 MPa after 10 cycles of thermal shock at 1200 °C. Such excellent thermal shock performance may be the result of the good interfacial bonding and the special gradient structure, the oxidation layer also plays a protective role.</p></span>
materials science, multidisciplinary,metallurgy & metallurgical engineering