Abstract:In order to improve the mechanical properties of TiAl alloys, TiAl composites with different solidification paths were synthesized by metallurgical method. Results show the TiC disappears and Ti2AlC increases when the Al content is more than 42% (at.%, similarly hereinafter). Small TiC particles are located in Ti2AlC grains with irregular shapes when the Al content is 40%, and they translate into clubbed Ti2AlC with increasing of Al. This metallurgy method can solve the defects of the Al lacking and the residual TiC. The g phase increases between lamellar colonies with the increasing of Al. When the Al content is 48%, the fully lamellar structure transforms into a duplex microstructure and there are small Ti2AlC phases in g phases, because the forming of Ti2AlC phase must consume Al. The compressive strength increases up to 1678.68 MPa as Al content is 46 at.%, and then decrease to 1460.22 MPa, the compressive strain increases and then keeps stabilization with the increasing Al. The maximum strength improves 38.82% and the maximum strain improves 121.37%. The Ti2AlC/TiAl composites fracture behaviors are load transferring behavior, crack deflection, trans-lamellar cracking and extraction of carbide reinforcements. The Ti2AlC phase and the fully lamellar structure improve the mechanical properties. (C) 2017 Elsevier Ltd. All rights reserved.

Microstructures of TiC-Al2O3-Fe composites prepared by SHS/PHIP

Investigation on microstructure of TiC-Fe cermets prepared by SHS/PHIP

PROPERTIES OF TiC-Al2O3/Fe COMPOSITES PREPARED BY SHS/PHIP

Microstructure and formation mechanism of TiC-30Fe cermet fabricated by SHS

Dense TiC-Al2O3 composites fabricated by SHS

Microstructure and resisting thermal shock behaviors of TiC-Al2O3/Fe functionally graded materials prepared by SHS/PHIP

Study on process and phase constitute of SHS of AlTiC composite

In situ synthesis and mechanical properties of bulk Ti3SiC2/TiC composites by SHS/PHIP

Influence Of Heat Treatment On The Microstructure And Properties Of Ti2alc By Shs/Phip

Investigation on NiAl–TiC–Al2O3 Composite Prepared by Self-Propagation High Temperature Synthesis with Hot Extrusion

Al3Ti/Al composites prepared by SHS

Growth Morphology and Microstructural Characterization of Nonstoichiometric Ti2alc Bulk Synthesized by Self-Propagating High Temperature Combustion Synthesis with Pseudo Hot Isostatic Pressing

Effects of Forming Conditions and TiC–TiB 2 Contents on the Microstructures of Self-Propagating High-Temperature Synthesized NiAl–TiC–TiB 2 Composites

DENSE TiC-Al2O3-Fe CERMET FABRICATED BY SHS

TiC-Fe cermets fabricated by SHS

Effect of Dispersed TiC Content on the Microstructure and Thermal Property of Shrouded-Plasma-Sprayed FeAl/TiC Composite Coatings

Densification, Microstructure and Mechanical Performance of TiC/Fe Composites by Spark Plasma Sintering

Microstructural Characterization of TiC in in Situ Synthesized Titanium Matrix Composites

In-situ Production and Microstructure of TiC/Fe_3Al Composites

Formation of TiC/Ti 2 AlC and Α 2 +γ in In-Situ TiAl Composites with Different Solidification Paths

In-situ TiC/Ti composites based on Ti 2 AlC–Ti system: Reaction process, microstructure, and mechanical properties