Abstract:This paper is concerned with obtaining metal-ceramic composite materials through the method of SHS compaction. The study investigates the influence of mechanical activation of metallic components in reactive mixtures based on the Ti + C + Cr + Ni system on the structure and properties of the resulting composites. Mechanical activation of the Ti, Cr, and Ni metallic powders was performed using two methods. In the first method, Cr and Ni powders were activated separately from the other components of the reactive mixtures using grinding media in a ball mill, after which they were mixed with Ti and carbon black powders. It was shown that the preliminary mechanical activation of the inert components reduces the combustion temperature and rate, which increases the average size of carbide grains. The second method involved a joint processing of Ti + Cr, Ti + Ni, and Ti + Cr + Ni powder mixtures in a ball mill, which were then mixed with carbon black. This method provided mechanical activation of titanium particles while minimizing the impact of grinding media on Cr and Ni powders. This led to an increase in the combustion rate and temperature, a decrease in the average size of carbide grains, and an improvement in the uniformity of the composite structure. A mechanism of interaction between the reagents (Ti + C) involving activated Cr and Ni particles in the combustion and structure formation zones is proposed. According to this mechanism, the mechanical activation of inert components leads to their direct participation in the reaction between titanium and carbon, which determines the reduction in combustion rate and temperature and affects the dispersion and uniformity of the structure of compact composites. The results were used to enhance the uniformity and refine the structure of the STIM-3B composite (synthetic hard tool material grade 3B).

THERMAL EXPANSION CHARACTERISTIC OF TiC- Ni CERMETS PREPARED BY SHS

Thermal physical properties of TiC-xNi cermets produced by combustion synthesis

MECHANICAL PROPERTIES OF TiC-Ni PRODUCED BY SHS AT ROOM AND HIGH TEMPERATURES

Research on TiC-Ni cermets by SHS and pseudo heat isostatic pressing

INFLUENCE OF Ni CONTENT ON TiC-Ni CERMETS BY SHS/PHIP

Investigation of TiC formation during ball-milling of elemental titanium and carbon

Investigation on microstructure of TiC-Fe cermets prepared by SHS/PHIP

TiC-Fe cermets fabricated by SHS

Computation and Analysis of Thermodynamics of Self-propagating High-temperature Synthesis TiC-Ni Cermets

DENSE TiC-Al2O3-Fe CERMET FABRICATED BY SHS

Combustion synthesis and densification of large-scale TiC–xNi cermets

Degassing Behavior and Solid State Reaction of Nano-Ti(Cn) Base Cermets in Sintering

Effect of WC Content on Thermal Shock Resistance of Ti(C,N)-based Cermets

Research on TiC-Ni-Mo Composites by Combustion Synthesis

EFFECT OF DILUENT CONTENT ON Si_3N_4-SiC-TiN CERAMICS PREPARED BY SELF-PROPAGATION HIGH-TEMPERATURE SYNTHESIS

Effects of WC/TiC addition on the thermodynamic behavior of TiB 2 -based cermet during sintering process

Combustion Synthesis of TiB-Ti Cermets

In-situ Combustion Synthesis and Densification of TiC–xNi Cermets

Synthesis of TiB 2 /Ti(C,N) cermet by RSPS: formation mechanism, shrinkage behavior, and mechanical properties

SHS Compaction of TiC-Based Cermets Using Mechanically Activated Mixtures

Study of Ti(C,N)-Based Cermets Fabricated by Pressureless-HIP Sintering