EFFECT OF DILUENT CONTENT ON Si_3N_4-SiC-TiN CERAMICS PREPARED BY SELF-PROPAGATION HIGH-TEMPERATURE SYNTHESIS

ZHANG Xuejun,ZHENG Yongting,HAN Jiecai,ZHOU Lijuan

2006-01-01

Abstract:Si3N4-SiC-TiN multiphase ceramic samples with a diameter of 24 mm were prepared with TiSi2 and SiC powders as the raw materials by the self-propagation high-temperature synthesis (SHS) method. The effect of different contents of diluent SiC in the samples on conversion percentage of reactant TiSi2 was calculated in theory and an SHS test was carried out. The results show that a certain degree of increase of SiC content was helpful for nitrification of TiSi2, and SiC particles were nitrified during the SHS process in the samples of green compacts with 40% (in mass, the same below) SiC and 50% SiC diluent. The TiSi2 reactants in the green compacts with 50% (in volume, the same below) porosity were fully nitrified and the final products were composed of Si3N4, SiC and TiN. Free silicon was detected in the 30% and 40% SiC-diluted samples with 45% porosity, while no free silicon was found in the 50% porosity green parts. Si3N4-SiC-TiN ceramic with a bending strength of 430 MPa and a fracture toughness of 3.6MPa·m1/2 was obtained after the SHS under a nitrogen pressure of 150 MPa and using a green compact with 35 % SiC diluent .