Abstract:The high-active sorbent for SO2 removal was developed by mixing CaO particles with fly ash in water at ambient temperature. The calcium utilization rate in the sorbent was achieved to 60% after the desulfurization reaction at 450 degrees C for 90 min, while the utilization rate for original pure CaO particles was only 21% under the identical conditions. The surface of the sorbent was examined by SEM, EDX, and BET analysis to study the activation mechanism. Results indicated that CaO particles were separated to several small particles of Ca(OH)(2) in water due to a significant heat release, while a small amount of Ca(OH)(2) dissolved in water. Under the condition of coexistence with fly ash particles, the tiny Ca(OH)(2) particles and its solute covered the surface of fly ash particles with the drying process. Therefore, SO2 could react efficiently with the Ca(OH)(2) on the surface of fly ash particles. XRD analysis showed that the composition of sorbent was not apparently changed in the sorbent preparation process. Moreover, the mixture time of CaO and fly ash in water did not play a significant role on calcium utilization rate. These results revealed that the hydration reactions between CaO and the materials such as SiO2 or Al2O3 in fly ash were limited in sorbent preparation process at ambient temperature. The IR analysis of reaction products indicated that gypsum could be produced efficiently at high reaction temperature by using the sorbent.

Study on desulfurization reaction characteristic of calcium-based sorbents

Effect of water content on desulfurization characteristic of calcium-based sorbent

Desulfurization Characteristic of Calcium-Based Sorbent During Activation Process.

Study on SO2 removal of calcium sorbent mixed with pulverized coal ash

Effects of additives on preparation and use of calcium sorbent for SO_2 removal

STUDY ON DESULFURIZATION CHARACTERISTIC IN CaO ACTIVATION REACTOR OF LIMESTONE INJECTION FGD SYSTEM --EXPERIMENTAL RESULTS AND DISCUSSION

Experimental study of steam reactivation of calcium-based sorbent for dry FGD process

Effect of Calcium Oxide Additive on the Performance of Iron Oxide Sorbent for High-Temperature Coal Gas Desulfurization

Two-Stage Desulfurization Of Calcium-Based Sorbents During Coal Combustion In The Chain-Grate Furnace

Nitrogen Dioxide Reaction With Calcium Based Sorbent During Dry Flue Gas Desulfurization

STUDY ON THE INFLUENCE OF MAGNGNE SIUM OXIDE UPON QUALITY OF HYDRATED LIME IN DRY FGD SYSTEM

An efficient calcium-based sorbent for flue gas dry-desulfurization: promotion roles of nitrogen oxide and oxygen

Experimental Study of the Mechanisms of Steam Reactivation of Unreacted Calcium-Based Sorbent for Flue Gas Desulphurisation

INTERACTION BETWEEN SO2 FROM FLUE GAS AND SORBENT PARTICLES IN DRY FGD PROCESSES

MECHANISM OF IMPROVING THE MEDIUM TEMPERATURE FGD PROCESS BY REACTIVATING SORBENTS BY STEAM

High Calcium Utilization and Gypsum Formation for Dry Desulfurization Process

DRY SO2 REMOVAL AT LOW TEMPERATURE USING CALCIUM-BASED SORBENTS

Kinetic model for desulfurization at medium temperature using hydrated absorbent

A THERMOGRAVIMETRIC STUDY ON SULFATION CHARACTERISTICS OF CALCIUM-BASED ABSORBENTS

Distributed pore model for sulfation of calcium-based sorbent

Effect of characteristic of sorbents on their sulfur capture capability at a fluidized bed condition