Abstract:WC reinforced WCu composites have excellent wear resistance and high-temperature strength, and can replace conventional WCu composites in special applications. In this work, WCu composites with core-shell structure are fabricated through a novel microwave-heating salt-bath carbonization (MSC) and infiltration method, using graphite as the carbon source. The MSC behavior of W particles and the influence of the graphite content on the microstructure and properties of the WCu composites are investigated. The results show that WC is successfully coated on the surface of W particles by the MSC method. The addition of an appropriate amount of graphite to W powders can improve the high-temperature mechanical properties and wear resistance of the WCu composites. Compared with conventional WCu composites, the WCu composites with 0.9 wt% graphite have higher thermal conductivity (245 W/(m·K)), higher hardness (293.8 HV), higher bending strength (1089.4 MPa), and higher compressive strength (410 MPa| 600°C ). The addition of graphite also significantly improved the wear resistance of the WCu composites. The average coefficient of friction (CoF) and wear rates (WR) of WCu9 composites are 0.51 and 5.37 × 10 −6 mm 3 N −1 m −1 , respectively. The WC reinforced WCu composites prepared in this work provide an excellent approach to improve the wear resistance and high-temperature properties of guide plates in guide devices.

Fabrication of Ni/WC composite with two distinct layers through centrifugal infiltration combined with a thermite reaction

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Dense Submicron-Sized ZrC – W Composite Produced by Reactive Melt in Fi Ltration at 1200 ° C

Fabrication and Micro-Structure of a Multilayer Functionally Graded (wc–co)–ni Composite

Fabrication of gradient WC-Ni cemented carbide materials by high gravity-assisted combustion synthesis and infiltration

Synthesis and fabrication of WC particulate reinforced Ni 3 Al intermetallic matrix composite coating by laser powder deposition

Preparation and characterization of high-performance in-situ synthesized WC reinforced nickel-based coatings

Fabrication of Hard Cermets by In-Situ Synthesis and Infiltration of Metal Melts into WC Powder Compacts

A novel approach to fabricate WC reinforced W Cu composites via MSC and infiltration method

Structural Evolution and Tribological Properties of WC Particles-Strengthened Nickel-Based Cladding Layers

Fabrication and Characterization of Tungsten Heavy Alloys with High W Content by Powder Metallurgy

Effect of Ni Content on Microstructure and Properties of WC-Ni Composites Prepared by Electroless Plating and Powder Metallurgy

Preparation and Characterization of Ni60-WC Composites Fabricated Using Laser Cladding Technique

High-Entropy-Alloy CoFeNiCr Bonded WC-Based Cemented Carbide Prepared by Spark Plasma Sintering

Study on the in-situ generation of hard phases and microstructural and mechanical properties in Ni-WC/W 2 C cladding layers prepared by TIG arc

Study on the friction and wear properties of nickel-based-WC-10Ni composite coatings prepared on the surface of TC4 titanium alloy

Fabrication and characterization of W/Cu/Ni-based high specific gravity alloy with Zr and Ti combined addition

Structure and Properties of WC-Fe-Ni-Co Nanopowder Composites for Use in Additive Manufacturing Technologies

Microstructural and Mechanical Characterization of Colloidal Processed WC/(W5Vol%Ni) via Spark Plasma Sintering

Study of Microstructure of Coarse-grain Tungsten Carbide Composite Produced by In-Situ Metallurgy Reaction

In-situ synthesis of core-shell structure W(WC) composite grains in W-Cu composites fabricated by infiltration