Abstract:Due to the extremely complex and strict service conditions of non-magnetic drill collars, the friction, wear and corrosion will lead to their damage and failure. Therefore, the surface modification technology can be used to substantially improve the surface performance and effectively extend the service life of non-magnetic drill collars. Under this engineering background, the laser cladding technology was employed to fabricate pure Inconel 625 and Inconel 625/WC coatings on the surface of TWZ-2 non-magnetic steel substrate, and the influences of WC content on the microstructure, phase composition, element distribution, microhardness and wear and corrosion resistance of these coatings were analyzed. The experimental results show that the microstructures of pure Inconel 625 and Inconel 625/WC coatings are all composed of planar grain, cellular grain, columnar grain and equiaxed grain successively. The phases of pure Inconel 625 coating are composed of γ-Ni phase and Laves phase. With WC particles mixed into Inconel 625 powder, various carbide phases appear in the composite coatings. The higher the WC content, the more the precipitated carbides formed by the reaction, thus aggravating the segregation of the solid solution strengthening elements. Besides, W and C elements present severe local segregation due to the undissolved WC particles. In terms of the hardening and strengthening effects of WC particles, the microhardness of the coatings gradually increases with the rise of WC content. The wear mechanisms of substrate and coatings are all compound wears, and different wear forms have different priorities. Accordingly, the wear mechanisms would change with the WC content. The higher the WC content, the lower the wear loss of coating, and the better the wear and friction resistance. Moreover, the corrosion resistance of coatings is better than that of substrate. With the increase of WC content, the corrosion resistance of the composite coatings decreases gradually.

Structural Evolution and Tribological Properties of WC Particles-Strengthened Nickel-Based Cladding Layers

Optimizing Wear Resistance and Tensile Strength of Nickel-Based Coatings through Tungsten Carbide Reinforcement

Study on the in-situ generation of hard phases and microstructural and mechanical properties in Ni-WC/W 2 C cladding layers prepared by TIG arc

Effect of WC on microstructure, molten pool and properties of Ni based coatings by multi-layer laser cladding

Investigation on the Ni60-WC composite coatings deposited by extreme-high-speed laser-induction hybrid cladding technology: Forming characteristics, microstructure and wear behaviors

Microstructure and properties of composite coatings by laser cladding Inconel 625 and reinforced WC particles on non-magnetic steel

Influence of WC ceramic particles on structures and properties of laser cladding Ni50-WC coatings

Experimental Study on the Microstructure and Tribological Properties of Laser-Clad Ni60-WC Composite Coatings

Comparative investigation on microstructures and properties of WC/Cr 3 C 2 reinforced laser cladding Ni-based composite coatings subjected to ultrasonic impact treatment

Study on Melting–Precipitation Evolution of WC in Ni/WC-12Co Coating during Laser Cladding and Tribological Properties

Microstructure and Wear Behavior of Hard Ni60 and Soft WC-12Co/Ni25 Coatings Prepared by Laser Cladding on W1813N Non-magnetic Stainless Steel

Influence of WC grain size on the microstructure and wear property enhancement of 18Ni300 coatings

Tribological Performance and Wear Mechanism of Laser Cladded NiCrAl-WC Coatings at High-Temperature

Effect of WC content on microstructure and properties of high-speed laser cladding Ni-based coating

Microstructure and Wear Behavior of Hard Ni60 and Soft WC-12Co/N125 Coatings Prepared by Laser Cladding on W1813N Non-magnetic Stainless Steel

Study on the friction and wear performance of laser cladding WC-TiC/Ni60 coating on the working face of shield bobbing cutter

Friction and wear behavior of Ni-based alloy coatings with different amount of WC–TiC ceramic particles

Preparation and Characterization of Ni60-WC Composites Fabricated Using Laser Cladding Technique

Microstructure evolution and tribological behavior of laser cladded Al 1.8 CrCuFeNi 2 /WC composite coatings on Ti-6Al-4 V

Research on the Preparation Process and Performance of a Wear-Resistant and Corrosion-Resistant Coating

Effect of WC Content on the Wear and Corrosion Properties of Oscillating Laser-Cladding-Produced Nickel-Based Coating