Abstract:(Ca,Dy) co-stabilized a-Sialon with elongated grains was prepared from SiO2-AlN-CaF2-Dy2O3 powders by carbothermal reduction-nitridation (CRN) at 1700 degrees C. Detailed investigations on the formation process of (Ca,Dy)-alpha-Sialon elongated grains performed under various firing conditions revealed that the big quartz particles were initially reduced and decomposed gradually by carbon, and a large number of ball-shaped particles consisting of amorphous (Si,Al,Ca,Dy)x(O,N)y were formed. With increasing temperature, nitrogen continuously diffused nto the liquid to form nitrogen-rich solid balls. Further increasing the temperature to 1700 degrees C and held for 2 h, hollow alpha-Sialon spheres with nanometric particles were obtained from nitrogen-rich solid balls. Subsequently, the framework structure of hollow spheres was destroyed at 1700 degrees C for 3 h, and (Ca,Dy)-alpha-Sialon grains grew up continuously by consuming nanometric particles in the rough interface via Ostwald ripening and growth stages moving on the smooth interface. Finally, (Ca,Dy)-alpha-Sialon developed well-defined crystalline elongated grains because the growth rate of rough surfaces is more rapid than that of smooth surfaces.

Effect of Y‐α‐Sialon Seeding and Holding Time on the Formation of Elongated (ca,dy)‐α‐sialon Crystals Prepared Via Carbothermal Reduction and Nitridation

Preparation and formation mechanism of elongated (Ca, Dy)-α-sialon powder via carbothermal reduction and nitridation

Preparation And Formation Mechanism Of Elongated (Ca,Dy)-Alpha-Sialon Powder Via Carbothermal Reduction And Nitridation

Synthesis of Rod-Like Α-Sialon by Carbothermal Reduction-Nitridation

Rapid Synthesis of Small Zeolite Y Crystals in the Absence of Seed Gel

Synthesis of α-Sialon by High Temperature Nitridation Reaction

Synthesis of alpha-Sialon by High Temperature Nitridation Reaction

Effects of Technical Parameters on the Phase Composition and Microstructure of Yb Α-Sialon Prepared by Combustion Synthesis

Combustion synthesis of rod-like Yb alpha-sialon powders

Effect of Diluents and NH4F Additive on the Combustion Synthesis of Yb Α-Sialon

Synthesis and characterization of single-crystalline phase Li-α-Sialon

Effects Of Technical Parameters On The Phase Composition And Microstructure Of Yb Alpha-Sialon Prepared By Combustion Synthesis

Synthesis And Characterization Of Single-Crystalline Phase Li-Alpha-Sialon

Study on Phase Transformation and Microstructure Development of Yb Α-Sialon Ceramics Prepared by Pressureless Sintering

Combustion Synthesis of Rod-Like Α-Sialon Seed Crystals

Effect of Alumina Contents on the Synthesis of ZrN-Sialon from Zircon

MICROSTRUCTURE CONTROL AND MECHANICAL PROPERTIES OPTIMIZATION OF Α-Sialon CERAMICS

Study on Synthesizing Diphase Sialon from Lower Al2O3 Bauxite by Carbothermal Reduction-Nitridation

Preparation of Β-Sialon from Fly Ash by Carbothermal Reduction-Nitridation Reaction

Microstructure and formation mechanism of combustion-synthesized rodlike Ca α-sialon crystals

Preparation and Characterization of Β-Sialon Ceramics from High Aluminium Fly Ash Via Carbothermal Reduction-Nitridation