Abstract:Yttrium-stabilized α -SiAlON powders with rod-like crystals were fabricated by combustion synthesis. Effects of starting compositions including relative content of diluents on final phase assemblage and grain morphology of combustion products were discussed. With appropriate proportions of α-SiAlON seeds and NH 4 F additive, α-SiAlON powders with rod-like crystals could be fabricated. It was found that the addition of α -SiAlON and NH 4 F could improve the anisotropic growth of rod-like crystals. However, if too much NH 4 F was added, the phase purity of combustion products would be decreased obviously and more β -SiAlON was produced. Additionally, the as-synthesized α -SiAlON powders were heat treated at 1800 °C for 1 h to examine their stability at the elevated temperature. The experimental results showed that after the heat treatment, single-phase α -SiAlON was obtained, revealing the high stability of combustion synthesized α -SiAlON powders.

Study On The Anisotropic Growth Of Rod-Like Yb Alpha-Sialon Crystals Prepared By Combustion Synthesis

Study on the anisotropic growth of rod-like Yb α-SiAlON crystals prepared by combustion synthesis

Combustion Synthesis of Rod-Like Α-Sialon Seed Crystals

Combustion synthesis of rod-like Yb alpha-sialon powders

Phase transformation and growth of rod-like α-SiAlON particles during combustion synthesis

Preparation of Ca α-SiAlON powders with rod-like crystals by combustion synthesis

Novel rod-like yttrium α-sialon crystalline powders prepared by combustion synthesis

Preparation of Y-SiAlON rod-like crystals and whiskers by combustion synthesis

Fabrication of yttrium-stabilized α -SiAlON powders with rod-like crystals by combustion synthesis

Combustion synthesis and sintering of rod-like Yb alpha-sialon powders

Fabrication of one-dimensional rod-like α-SiAlON powders in large scales by combustion synthesis

Effects of starting compositions on the phase composition and microstructure of Yb α-SiAlON prepared by combustion synthesis

Microstructure and formation mechanism of combustion-synthesized rodlike Ca α-sialon crystals

Growth Mechanism of Crystalline Sialon Microtubes Prepared by Combustion Synthesis

Fabrication of Yb alpha-SiAlON ceramics by SPS with crystal seeds prepared through combustion synthesis

Effect of Nitrogen Pressure and Additives on Combustion Synthesis of Rod-Like Yttrium α-SiAlON Crystals

Combustion synthesis and sintering of rod-like Yb α-Sialon powders

Novel Faceted alpha-SiAlON Micro-Crystals Prepared by Combustion Synthesis

Effects Of Technical Parameters On The Phase Composition And Microstructure Of Yb Alpha-Sialon Prepared By Combustion Synthesis

Study on Phase Transformation and Microstructure Development of Yb Α-Sialon Ceramics Prepared by Pressureless Sintering

Growth mechanism of Y α-SiAlON whiskers prepared by combustion synthesis