Abstract:AlN-SiC solid solution particles with a variety of morphologies including faceted polyhedrons with or without ledges; hexagonal platelets; hexagonal columns with a hexagonal plate or a pyramidal cap; and interpenetrating cones, have been found in the combustion products of a mixture of Al, Si, and carbon black under a nitrogen pressure of 10 MPa. Combustion temperature (the growth temperature of crystals) is the most important factor controlling the morphology of crystals formed in the combustion product. When temperatures are close to the melting point of the solid solutions, a small driving force for nucleation and long distances of surface migration make nucleation on the basal plane difficult, and thus the solid solution particles tend to grow as platelets. Supersaturation is the second key factor influencing crystal growth. At relatively low temperatures, a low supersaturation at the large pores renders nucleation difficult and the solid solution particles tend to grow as platelets. At relatively low temperatures and high supersaturation, a relatively high driving force for nucleation and short mean distances of surface migration promote the growth of AlN-SiC solid solutions as polyhedrons. The formation of the ledges on the polyhedral particles is attributed to the differences in the evaporation rates and the deposition rates between Al and Si. At relatively low temperatures and an intermediate supersaturation, the solid solution particles grow as prismatic columns. The formation of the prismatic columns with a hexagonal plate, or a pyramidal cap, is attributed to a sudden change of temperature during combustion. A possible growth mechanism for the AlN-SiC solid solution cones is proposed.

Novel Faceted alpha-SiAlON Micro-Crystals Prepared by Combustion Synthesis

Preparation of Ca α-SiAlON powders with rod-like crystals by combustion synthesis

Formation of β-SiAlON micropalings consisting of nanorods during combustion synthesis

Preparation of Y-SiAlON rod-like crystals and whiskers by combustion synthesis

Phase transformation and growth of rod-like α-SiAlON particles during combustion synthesis

Combustion Synthesis of Rod-Like Α-Sialon Seed Crystals

Study on the anisotropic growth of rod-like Yb α-SiAlON crystals prepared by combustion synthesis

Combustion Synthesis of β-Si<sub>3</sub>N<sub>4</sub> and β-SiAlON with Elongated Prismatic Micro-Crystals by Adding SrCO<sub>3</sub> and NH<sub>4</sub>F

Fabrication of yttrium-stabilized α -SiAlON powders with rod-like crystals by combustion synthesis

Study On The Anisotropic Growth Of Rod-Like Yb Alpha-Sialon Crystals Prepared By Combustion Synthesis

Growth Mechanisms for SiC-AlN Solid Solution Crystals Prepared by Combustion Synthesis

Solid-state NMR and XRD study of α-SiAlON powders prepared by combustion synthesis

Combustion Synthesis Of Beta-Si3n4 And Beta-Sialon With Elongated Prismatic Micro-Crystals By Adding Srco3 And Nh4f

Growth Mechanism of Crystalline Sialon Microtubes Prepared by Combustion Synthesis

Fabrication of one-dimensional rod-like α-SiAlON powders in large scales by combustion synthesis

Growth mechanism of Y α-SiAlON whiskers prepared by combustion synthesis

Effects of starting compositions on the phase composition and microstructure of Yb α-SiAlON prepared by combustion synthesis

Microstructure and formation mechanism of combustion-synthesized rodlike Ca α-sialon crystals

Combustion Synthesis of Β-Sialon Whiskers

Novel rod-like yttrium α-sialon crystalline powders prepared by combustion synthesis

Synthesis and Characterization of Several alpha-Silicon Nitride Nanostructures