Abstract:The growth mechanism and morphologies of AlN whiskers prepared by the carbothermal reduction method are studied as well as the technological condition. All experiments were carried out in a vertical, controlled-atmosphere, graphite element resistance furnace. The reactor chamber volume is Φ250×210 mm, and the reactant weight is about 20 g each times (it contains about 70 wt.% Al2O3). Nitrogen pressure in the furnace is 0.1 MPa (1 atm). The optimum growth condition is at 1700°C for 5 h with flowing nitrogen (0.6 l min−1), when the raw materials are α-Al2O3 and graphite (Al2O3:C=4:1 in weight). The yield of AlN whiskers is about 3–5 g each time, and 50 wt.% or more of Al2O3 can convert to AlN whiskers. Generally, whiskers with hexagonal cross section grow along 〈0001〉 and plate-like whiskers have a growth orientation parallel to 〈0111〉 et al other than 〈0001〉. During the growth of whiskers, the VLS mechanism and VS mechanism serve the function together. In the early stage, α-Al2O3 will react with CaO to form Ca-aluminates such as CaO·6Al2O3(CA6), CaO·2Al2O3(CA2), CaO·Al2O3 (CA). These Ca-aluminates can provide liquid catalysts for the nucleation of AlN whiskers. After that, the AlN whiskers will grow out from the substrate surface by the VS mechanism. As proximity to substrate surface, there is less growth space and higher supersaturation, and far from substrate surface, there is large growth space and low supersaturation. So near the substrate surface AlN whiskers are small and with irregular shape. Far from the substrate surface, AlN whiskers are sensibly straight and with regular shape.

Growth mechanism of Y α-SiAlON whiskers prepared by combustion synthesis

Preparation of Y-SiAlON rod-like crystals and whiskers by combustion synthesis

Formation of Yb α-SiAlON whiskers by heat treatment of hot-pressed bulk samples

Combustion Synthesis of Β-Sialon Whiskers

Study on the anisotropic growth of rod-like Yb α-SiAlON crystals prepared by combustion synthesis

Investigation On Combustion Synthesis Of Aln Whisker

Combustion Synthesis of AlN Whiskers

Phase transformation and growth of rod-like α-SiAlON particles during combustion synthesis

A New Route to Synthesize SiC−AlN Solid Solution Whiskers

Fabrication of yttrium-stabilized α -SiAlON powders with rod-like crystals by combustion synthesis

Thermodynamics and Kinetic Considerations behind the Growth of AlN Whiskers Synthesized by Carbothermal Reduction

Growth of platelike and branched single-crystalline Si3N4 whiskers

Preparation of Ca α-SiAlON powders with rod-like crystals by combustion synthesis

Study On The Anisotropic Growth Of Rod-Like Yb Alpha-Sialon Crystals Prepared By Combustion Synthesis

Synthesis mechanism of α-Si3N4 whiskers via SiO vapor in reaction bonded Si3N4-SiC composite

Fabricaion process and growth characteristics of A1N whiskers by sublimation-recrystallization method

Morphologies and growth mechanisms of aluminium nitride whiskers

Morphologies and Growth Mechanisms of Aluminum Nitride Whiskers Synthesized by Carbothermal Reduction

Fabrication of one-dimensional rod-like α-SiAlON powders in large scales by combustion synthesis

The Preparation and Characterization of Β-Sialon NanostructureWhiskers

A Novel Whisker of α-MoO 3 : Characterization and Growth Mechanism