Abstract:(Ca,Dy) co-stabilized a-Sialon with elongated grains was prepared from SiO2-AlN-CaF2-Dy2O3 powders by carbothermal reduction-nitridation (CRN) at 1700 degrees C. Detailed investigations on the formation process of (Ca,Dy)-alpha-Sialon elongated grains performed under various firing conditions revealed that the big quartz particles were initially reduced and decomposed gradually by carbon, and a large number of ball-shaped particles consisting of amorphous (Si,Al,Ca,Dy)x(O,N)y were formed. With increasing temperature, nitrogen continuously diffused nto the liquid to form nitrogen-rich solid balls. Further increasing the temperature to 1700 degrees C and held for 2 h, hollow alpha-Sialon spheres with nanometric particles were obtained from nitrogen-rich solid balls. Subsequently, the framework structure of hollow spheres was destroyed at 1700 degrees C for 3 h, and (Ca,Dy)-alpha-Sialon grains grew up continuously by consuming nanometric particles in the rough interface via Ostwald ripening and growth stages moving on the smooth interface. Finally, (Ca,Dy)-alpha-Sialon developed well-defined crystalline elongated grains because the growth rate of rough surfaces is more rapid than that of smooth surfaces.

Microstructure and formation mechanism of combustion-synthesized rodlike Ca α-sialon crystals

Preparation of Ca α-SiAlON powders with rod-like crystals by combustion synthesis

Novel rod-like yttrium α-sialon crystalline powders prepared by combustion synthesis

Combustion Synthesis of Rod-Like Α-Sialon Seed Crystals

Study On The Anisotropic Growth Of Rod-Like Yb Alpha-Sialon Crystals Prepared By Combustion Synthesis

Combustion synthesis of rod-like Yb alpha-sialon powders

Growth Mechanism of Crystalline Sialon Microtubes Prepared by Combustion Synthesis

Fabrication of one-dimensional rod-like α-SiAlON powders in large scales by combustion synthesis

Structural Formation and Mechanism in Combustion Synthesis of Nitrogen Ceramics (AIN, Si<sub>3</sub>N<sub>4</sub> and AIN-SiC)

Synthesis of Rod-Like Α-Sialon by Carbothermal Reduction-Nitridation

Preparation of Y-SiAlON rod-like crystals and whiskers by combustion synthesis

Phase transformation and growth of rod-like α-SiAlON particles during combustion synthesis

Study on the anisotropic growth of rod-like Yb α-SiAlON crystals prepared by combustion synthesis

Combustion synthesis and sintering of rod-like Yb α-Sialon powders

Fabrication of yttrium-stabilized α -SiAlON powders with rod-like crystals by combustion synthesis

Preparation and formation mechanism of elongated (Ca, Dy)-α-sialon powder via carbothermal reduction and nitridation

Combustion synthesis and sintering of rod-like Yb alpha-sialon powders

Fabrication of (ca + Yb)- and (ca + Sr)-stabilized Α-Sialon by Combustion Synthesis

Preparation And Formation Mechanism Of Elongated (Ca,Dy)-Alpha-Sialon Powder Via Carbothermal Reduction And Nitridation

Novel Faceted alpha-SiAlON Micro-Crystals Prepared by Combustion Synthesis

Combustion Synthesis Of Beta-Si3n4 And Beta-Sialon With Elongated Prismatic Micro-Crystals By Adding Srco3 And Nh4f