Rapid Synthesis of Small Zeolite Y Crystals in the Absence of Seed Gel

YUAN Hao,LI Gang

DOI: https://doi.org/10.3969/j.issn.1001-8719.2012.06.019

2012-01-01

Abstract:Effects of n(Na2O)/n(SiO2),n(SiO2)/n(Al2O3) and Si source on the crystallization process of zeolite Y and its particle size were investigated in the absence of both seed gel and organic templates.The results showed that increase of n(Na2O)/n(SiO2) in zeolite Y synthesis system not only promoted the formation of zeolite Y crystals,but also facilitated transformation of zeolite Y into other zeolite.The particle size and n(SiO2)/n(Al2O3) of zeolite Y decreased with the increase of n(Na2O)/n(SiO2) in the synthesis system.The average particle sizes of zeolite Y were 0.4 and 0.3 μm,respectively,under n(Na2O)/n(SiO2) of 0.60 and 0.88 and crystallized for 3 h at 100℃.The small crystals already crystallized will aggregate into large ones under n(Na2O)/n(SiO2) of 1.04.A wide particle size distribution(0.2-0.7 μm) and the decrease of n(SiO2)/n(Al2O3) in zeolite Y were observed with the decrease of n(Na2O)/n(SiO2).The particle size distribution of zeolite Y was narrow(0.3-0.5 μm) when colloidal silica sol or nanometer silica powder was used as Si source,while a wide particle size distribution(0.2-1.0 μm) was observed when sodium silicate was used as Si source.