Abstract:Nano-sized crystals of alpha calcium sulfate hemihydrate (α-HH) with considerable morphology-dependent properties find promising applications in the clinical fields as a cementitious material. Towards this end, ultrasound-assisted rhamnolipid and surfactin biosurfactant-template route is explored to control the morphology and aspect ratio of nano-CaSO4 by adjusting the mass ratio of rhamnolipid/H2O, surfactin/H2O and rhamnolipid/surfactin. The change in the molar ratio of [SO4(2-)]:[Ca(2+)] results in modification in variable morphology and size of nano-CaSO4 including long, short rods and nanoplates. With increase in the rhamnolipid/H2O ratio from 1.3 to 4.5, the crystal length decreases from 3 μm to 600 nm with the corresponding aspect ratio reduced sharply from 10 to 3. Similarly, the crystal morphology gradually changes from submicrometer-sized long rod to hexagonal plate, and then plate-like appearance with increase in surfactin concentration. The preferential adsorption of rhamnolipid on the side facets and surfactin on the top facets contributes to the morphology control. The process using 50% amplitude with a power input of 45.5 W was found to be the most ideal as observed from the high yields and lower average l/w aspect ratio, leading to more than 94% energy savings as compared to that utilized by the conventional process. As a morphology and crystal habit modifier, effects of Mg(2+) and K(+) ions on α-HH growth were investigated to find an optimal composition of solution for α-HH preparation. Mg(2+) ions apparently show an accelerating effect on the α-HH growth; however, the nucleation of α-HH is probably retarded by K(+) ions. Thus, the present work is a simple, versatile, highly efficient approach to controlling the morphology of α-HH and thereby, offers more opportunities for α-HH multiple applications.

α-Calcium Sulfate Hemihydrate Nanorods Synthesis: A Method for Nanoparticle Preparation by Mesocrystallization

Controlled synthesis of monodisperse alpha-calcium sulfate hemihydrate nanoellipsoids with a porous structure

Synthesis of α-calcium sulfate hemihydrate submicron-rods in water/n-hexanol/CTAB reverse microemulsion

Formation of spherical calcium sulfate mesocrystals: orientation controlled by subunit growth

Facile Synthesis and Properties Research of Single Crystal Calcium Sulfate Nanotubes Through Reverse Micelle Method

Microemulsion Synthesis of Nanosized Calcium Sulfate Hemihydrate and Its Morphology Control by Different Surfactants.

A Facile Method to Control the Structure and Morphology of Α-Calcium Sulfate Hemihydrate

Ultrasound-assisted/biosurfactant-templated size-tunable synthesis of nano-calcium sulfate with controllable crystal morphology

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

Aqueous Preparation of Highly Dispersed Hydroxyapatite Nanorods for Colloidal Liquid Crystals

Controllable synthesis of snowflake‐like α‐calcium sulfate hemihydrate microstructures using Na2EDTA as morphology modifier

Control of α-calcium sulfate hemihydrate morphology using reverse microemulsions

Synthesis of Monodisperse Spherical Nano Alumina by Hydrothermal Method and Its Mechanism Study

Α-Fe2o3 Nanocrystals: Controllable SSA-Assisted Hydrothermal Synthesis, Growth Mechanism, and Magnetic Properties

A Simple and Effective Route for the Synthesis of Crystalline Silver Nanorods and Nanowires

Economical and Simple Fabrication of Rod-Like Hydroxyapatite Nanocrystal with Good Dispersity and Crystallinity

Hydrothermal Microemulsion Synthesis of Stoichiometric Single Crystal Hydroxyapatite Nanorods with Mono-Dispersion and Narrow-Size Distribution

Synthesis of single-crystal HAP nanorods

Direct Synthesis of Hollow Vaterite Nanospheres from Amorphous Calcium Carbonate Nanoparticles via Phase Transformation

Colloidal Preparation Of Monodisperse Nanocrystals

Facile synthesis and photoluminescence of calcium sulphate nanorods