Effect of Calcium to Silicon Ratio on the Microstructure of Hydrated Calcium Silicate Gels Prepared under Medium Alkalinity
Haojing Ba,Jiajie Li,Wen Ni,Ying Li,Yongjian Ju,Ben Zhao,Guoping Wen,Michael Hitch
DOI: https://doi.org/10.1016/j.conbuildmat.2023.131240
2022-01-01
Abstract:The hydration of solid waste cementitious materials has a medium alkalinity and low calcium-to-silicate ratio (Ca/Si). Understanding how the hydration products behave in such a system is very important to optimize and create new solid waste cementitious materials. This paper investigates the effect of Ca/Si on the generated C-S-H gels under medium alkalinity. C-S-H gels were prepared by the double decomposition method at room temperature, and XRD, SEM, TG-DSC, XPS, and NMR examined the microstructure of C-S-H gels. Results show that the Cl- concentration in the solution controlled its pH, ranging between 11.1 and 12.8. However, the Ca/Si of C-S-H gels increased with the initial Ca/Si in solution. However, it couldn't increase higher than 0.8 when the C-S-H was synthesized at a pH of about 12. With the increase in Ca/Si, the agglomeration of C-S-H gels increased, and the C-S-H became crystallized, the temperature of beta -wollastonite formation enhanced. However, the beta -wollastonite formation temperature of C-S-H gel synthesized under medium alkalinity was lower than that under high alkalinity. The increase in the Ca/Si of C-S-H gel decreased the Q3 type tetrahedra formation and increased the Q2 type tetrahedra formation. The variation of H2O/Si is related to the amount of Q2 and Q3 type tetrahedra in the C-S-H gel, which is determined by the synthesis method. Medium alkalinity could assist in generating C-S-H gel with low Ca/Si and high MCL. The results of this study could guide new solid wasted-based contentious materials production.