Poly(propylene carbonate)/clay nanocomposites with enhanced mechanical property, thermal stability and oxygen barrier property
Dexiu Wang,Jinyang Li,Xiaocheng Zhang,Jinming Zhang,Jian Yu,Jun Zhang
DOI: https://doi.org/10.1016/j.coco.2020.100520
IF: 8
2020-12-01
Composites Communications
Abstract:<p>To develop eco-polymeric materials is of significant importance to protect the global environment and promote the sustainable development of human society. Poly (propylene carbonate) (PPC) as a new biodegradable polymer has attracted much interest, but some properties of PPC have to be improved before the practical utilization.</p><p>In this work, the re-dispersible unmodified laponite and montmorillonite (MMT) were used as the nanometer reinforcing phase to enhance the mechanical property, thermal stability and oxygen barrier property of PPC. Via a simple solution mixing method, the PPC/laponite and PPC/MMT nanocomposites were fabricated. The unmodified laponite and MMT were well dispersed in the PPC matrix, which was confirmed by TEM results. As a result, the obtained PPC/clay nanocomposites exhibited high transparency (>80%) and enhanced storage modulus (100–150% higher than PPC), when the clay content was in a range of 1–10 wt%. In addition, the incorporation of lower than 3 wt% of laponite and MMT increased the elongation at break and thermal stability of PPC. The initial decomposition temperature (T<sub>d10%</sub>) of PPC/clay nanocomposites with 1 wt% clay was approximately 250 °C, which was substantially higher than that of pure PPC (215 °C). The PPC/clay nanocomposites with 7 wt% clay displayed the lowest O<sub>2</sub> permeability, which was two orders of magnitude lower than that of pure PPC. Therefore, the resultant PPC/clay nanocomposites with enhanced properties have a potential to boost the practical utilization of PPC.</p>
materials science, composites