Abstract:A series of transition metal‐doped TiO2 was prepared by a simple sol‐solvothermal method. Ag−TiO2 was chosen for further study due to its extraordinary reactivity. Ag−TiO2 produces more ⋅O2− and ⋅OH under visible light, which are responsible for the oxidation of methyl orange to CO2 and H2O and other inorganic small molecules. In this study, a series of transition metal‐doped TiO2 was prepared by a simple sol‐solvothermal method. Mix an ethanol solution of tetrabutyl titanate and metal nitrate solution to obtain a homogeneous sol, which is then subjected to solvothermal treatment. After calcination, the metal‐TiO2 naoncomposite was obtained. Selected transition metal precursors, including Cu, Fe, Ag, Cr, Co and Zn, were doped into TiO2 nanocatalysts to assess photocatalytic degradation activities. The results show that 1 mol % Ag−TiO2 photocatalyst has a larger specific surface area, a stable anatase phase and the narrowest forbidden band energy (3.00 eV). In photocatalytic degradation of methyl orange (MO) tests, 1 mol % Ag−TiO2 could reach 100 % decolourisation after 70 min and 75.43 % mineralisation after 90 min. ESR analysis confirmed that Ag doping significantly increased the content of ⋅O2− and ⋅OH for the TiO2 catalyst, which are responsible for the oxidation reactions and consequently degradation of pollutants. The photocatalytic degradation mechanism of MO was also proposed. The TOC analyses confirmed the mineralization of MO. The excellent thermal and chemical stability of 1 mol % Ag−TiO2 has also been demonstrated by thermogravimetric analysis and cycling experiments. Electrochemical tests have also demonstrated the excellent electrochemical properties of 1 mol % Ag−TiO2.

Preparation and characterization of the nanometer TiO2 immobilized on macro-porous-resin

Preparation of TiO_2/SiO_2 and Photo-Catalytic Degradation of Methyl-Orange

TiO2 Nanoparticles Supported on PMMA Nanofibers for Photocatalytic Degradation of Methyl Orange

Nanoporous core–shell Cu@Cu2O nanocomposites with superior photocatalytic properties towards the degradation of methyl orange

Photodegradation of an Azo Dye Using Immobilized Nanoparticles of TiO2 Supported by Natural Porous Mineral.

Composite of TiO2 Nanoparticles and Carbon Nanotubes Loaded on Poly(methyl Methacrylate) Nanofibers: Preparation and Photocatalytic Performance

Preparation and characterization of nano-TiO;/diatomite photocatalyst for photocatalytic degradation of dimethylamine（DMA）

Facile Synthesis and Photocatalytic Properties of TiO2 Nanoparticles Supported on Porous Glass Beads

Preparation and Photocatalytic Properties of Fe(III)-Grafted TiO<sub>2</sub> Nano-Composite Powders

Fabrication and Characteristics of TiO2-ZnO Macroporous Composite Nanomaterials

Photo-Catalytic Activity And Life Time Of The Tio2 Nano-Particles

Fabrication of TiO2-containing Nanocomposite Films and Their Photocatalytic Degradation for Methyl Orange

Characterization and Photocatalytic Activity of Poly(3-Hexylthiophene)-Modified Tio2 for Degradation of Methyl Orange under Visible Light

Controlled hydrolytic synthesis of nanosized titania and evaluation of photodegradation of methyl orange

Enhanced Photocatalytic Degradation of Methyl Orange by Metal‐Tio2 Nanoparticles

Preparation and Photocatalytic Performance of Sodium Alginate/Polyacrylamide/Polypyrrole-TiO2 Nanocomposite Hydrogels

Enhanced Photocatalytic Degradation of Methyl Orange Using Nitrogen‐Functionalized MesoporousTiO2 Decorated with Au9 Nanoclusters

Template‐Directed Fabrication of Anatase TiO2 Hollow Nanoparticles and Their Application in Photocatalytic Degradation of Methyl Orange

Green synthesized nano-TiO2 from Tamarindusindica leaf extract for photo-degradation of combination of dyes by suspension and immobilization on inert supports

Preparation of Titania Nanotube and Its Photocatalytic Performance for MB Photo-Degradation

Photocatalytic degradation of methyl orange in aqueous suspension of mesoporous titania nanoparticles