Abstract:Titania nanotubes (TNTs) were synthesized by hydrothermal treatment of rutile-phase TiO2 nanoparticals in NaOH solution at 110 degrees C for 24 hours. After drying in aceton for 36 h, the TNTs were under vacuum drying for 24 h at room temperature. The Pt-inserted titania nanotubes (Pt/TNTs) were obtained by filling H2 PtCl6 ethanol solution into the TNTs after vacuum drying. The characterizations of the as-synthesized samples were confirmed by TEM, XRD, and UV-Vis. The photocatalytic activity of the Pt/TNTs was investigated by photo-induced decomposition of methyl orange(MO)under the main 365 nm UV-light. In order to comparison, the photocatalytic activity of both the rutile-phase TiO2 nanoparticles and pure TNTs were also investigated at the same time under the same experimental conditions. The TEM images show that the TNTs are hollow, a few hundred nanometers long, and the inner/outer diameter is about 6/10 nm. The crystal structure of TNTs is H2Ti2O5 x H2O with a little Na. Both the shape and the crystalline of the TNTs are not changed after the modification. The oval or round Pt0 nanoparticals, about 3 nm in diameter, are found only in the nanotubes. Pt/TNTs exhibit enhanced absorption at the visible range in the UV-Vis spectra and its start absorption band edge(lambda0 approximately 457 nm)is obviously redshifted compared to the rutile-phase TiO2 nanoparticals and pure TNTs. The Pt nanoparticles are found to significantly enhance the photocatalytic activity of TNTs. Pt/TNTs are demonstrated to be highly efficient for the UV-light induced photocatalytic decomposition of MO compared to both the rutile-phase TiO2 nanoparticals and pure TNTs. After irradiation for 60 min, the photocatalysis decomposition rate of MO in rutile-phase TiO2 nanoparticals, TNTs and Pt/TNTs are 46.8%, 57.2% and 84.6% respectively.

Preparation of Titania Nanotube and Its Photocatalytic Performance for MB Photo-Degradation

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

The preparation and TiO_2 nanotubes photocatalytic degradation of methyl orange research

Preparation and Photocatalytic Performance of Titania Nanotubes Loaded with Ag Nanoparticles

Study on preparation and photocatalytic performance of TNT photoelectrodes prepared under different conditions

Fabrication and Photocatalytic Activity of Pt-Inserted Titania Nanotubes

Photocatalytic Activity of Nitrogen Doped Nano-titanias and Titanium Nitride towards Methylene Blue Decolouration

Characterization, Properties and Catalytic Application of TiO2 Nanotubes Prepared by Ultrasonic-Assisted Sol-Hydrothermal Method

Photocatalytic degradation of selected dyes by titania thin films with various nanostructures

Preparation of Ag-doped Titania Nanotube and Its Photocatalytic Degradation Performance for Nitrobenzene Wastewater

The effect of the preparation conditions on the photo-electrocatalytic performance of titania nanotubes

A study on the preparation and photocatalytic performance of ZnO/TiO2 nanotubes

Adsorption and photocatalytic degradation of methylene blue using high surface area titanate nanotubes (TNT) synthesized via hydrothermal method

Enhanced Photoelectrocatalytic Degradation of Organic Pollutants Using TiO2 Nanotubes Implanted with Nitrogen Ions

Preparation and Characterization of Titanate Nanotubes by Hydrothermal Method

Preparation and performance of Pd nano-crystallite decorated TiO_2 nano-tubes arrays photoelectrode

Comparative study of photocatalytic performance on different TiO 2 nano-tubes arrays

[Research of the Photoelectrocatalysis Degradation of Methylene Blue of TiO2 Nanotube Array Films Annealed in Oxygen Atmospheres].

High Photocatalytic and Adsorptive Performance of Anatase-Covered Titanate Nanotubes Prepared by Wet Chemical Reaction

EFFECTS OF CALCINATION TEMPERATURES ON THE STRUCTURE AND ADSORPTION BEHAVIOR OF TITANIA NANOTUBE

Combined Potential of Three Catalysis Types on TiO2 Nanotube (tnt)/ti and Nanoparticle (tnp)/ti Photoelectrodes: A Comparative Study