Abstract:Titania nanotubes (TNTs) were synthesized by hydrothermal treatment of rutile-phase TiO2 nanoparticals in NaOH solution at 110 degrees C for 24 hours. After drying in aceton for 36 h, the TNTs were under vacuum drying for 24 h at room temperature. The Pt-inserted titania nanotubes (Pt/TNTs) were obtained by filling H2 PtCl6 ethanol solution into the TNTs after vacuum drying. The characterizations of the as-synthesized samples were confirmed by TEM, XRD, and UV-Vis. The photocatalytic activity of the Pt/TNTs was investigated by photo-induced decomposition of methyl orange(MO)under the main 365 nm UV-light. In order to comparison, the photocatalytic activity of both the rutile-phase TiO2 nanoparticles and pure TNTs were also investigated at the same time under the same experimental conditions. The TEM images show that the TNTs are hollow, a few hundred nanometers long, and the inner/outer diameter is about 6/10 nm. The crystal structure of TNTs is H2Ti2O5 x H2O with a little Na. Both the shape and the crystalline of the TNTs are not changed after the modification. The oval or round Pt0 nanoparticals, about 3 nm in diameter, are found only in the nanotubes. Pt/TNTs exhibit enhanced absorption at the visible range in the UV-Vis spectra and its start absorption band edge(lambda0 approximately 457 nm)is obviously redshifted compared to the rutile-phase TiO2 nanoparticals and pure TNTs. The Pt nanoparticles are found to significantly enhance the photocatalytic activity of TNTs. Pt/TNTs are demonstrated to be highly efficient for the UV-light induced photocatalytic decomposition of MO compared to both the rutile-phase TiO2 nanoparticals and pure TNTs. After irradiation for 60 min, the photocatalysis decomposition rate of MO in rutile-phase TiO2 nanoparticals, TNTs and Pt/TNTs are 46.8%, 57.2% and 84.6% respectively.

Characterization, Properties and Catalytic Application of TiO2 Nanotubes Prepared by Ultrasonic-Assisted Sol-Hydrothermal Method

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Preparation and Characterization of Titanate Nanotubes by Hydrothermal Method

Synthesis, Characterization, and Photocatalytic Activity of N-Doped TiO2 Nanotubes

Preparation of Titania Nanotube and Its Photocatalytic Performance for MB Photo-Degradation

Study on photocatalytic property of TiO2 nanotubes

Visible Light-Driven Iodine-Doped Titanium Dioxide Nanotubes Prepared by Hydrothermal Process and Post-Calcination

A study on the preparation and photocatalytic performance of ZnO/TiO2 nanotubes

A Review on Tio2-Based Nanotubes Synthesized Via Hydrothermal Method: Formation Mechanism, Structure Modification, and Photocatalytic Applications

Synthesis, characterization, and photocatalytic activities of titanate nanotubes surface-decorated by zinc oxide nanoparticles

Formation and Photo-Degradation Performance of Titania Nanotubes

Synthesis and characterization of WO3/titanate nanotubes nanocomposite with enhanced photocatalytic properties

Fabrication and Characterization of TiO2/short MWNTs with Enhanced Photocatalytic Activity

Fabrication and Photocatalytic Activity of Pt-Inserted Titania Nanotubes

The Fabrication and Characterization of Novel Carbon Doped TiO2nanotubes, Nanowires and Nanorods with High Visible Light Photocatalytic Activity

Synthesis, Characterization of Cr-doped TiO 2 Nanotubes with High Photocatalytic Activity

Preparation,Characterization of Si Doped TiO_2 Nanotubes and Its Application in Photocatalytic Oxidation of VOCs

Preparation and Photocatalytic Performance of Titania Nanotubes Loaded with Ag Nanoparticles

Preparation and characterization of titanium oxide nanotubes

Synthesis, Characterization and Performance of Ternary Doped Cu–Ce–B/TiO2 Nanotubes on the Photocatalytic Removal of Nitrogen Oxides

Synthesis of Titania and Titanate Nanomaterials and Their Application in Environmental Analytical Chemistry.