Preparation and characterization of organic modified montmorillonite/polylactic acid nanocomposites

Yanmei Zuo,Zhisheng Fu,Zehui Jiang

DOI: https://doi.org/10.13416/j.ca.2017.09.007

2017-01-01

Abstract:With PLA(polylactic acid) as matrix,CTAB(cetyl trimethyl ammonium bromide) with CEC(cation exchange capacity) at 0.5 or 1.0 as modifiers of NMMT[sodium MMT (montmorillonite)],the CMMT(CEC modified MMT) was prepared.Then,the TFC (secondary modified MMT)was prepared by CTS (chitosan) modified CMMT.Finally,the PLA/CMMT and PLA/TFC nanocomposites were prepared by melting intercalation method.The research results showed that the characteristic peak of modifier appear in FT-IR (infrared spectra) of CMMT and TFC,and the X-ray diffraction peak moves to the left,which indicates that the interlayer spacing of TFC and CMMT is larger than that of NMMT.The modified PLA has the good physical and mechanical properties,but the reunion phenomenon is more serious with increasing modified NMMT content in system.The nanocomposite had the relatively best combination property when mass fraction of modified NMMT was 3％ in total raw materials,and it has the good environmental protection,compatibility,biodegradable and other advantages.