Preparation and Properties of PA6/Epoxy-resin-modified Montmorillonite Nanocomposites
ZHOU Xueqin,SHENG Zhongyi,XIE Songgui,SHENTU Baoqing,WENG Zhixue
DOI: https://doi.org/10.19491/j.issn.1001-9278.2010.02.009
2010-01-01
Abstract:Montmorillonite (MMT) was modified by epoxy resin leading to organic montmorillonite (OMMT),whose interlayer spacing increased from 1.22 nm to 5.13 nm. OMMT was dispersed into PA6 as nano-scale particles forming nanocomposites. X-ray diffraction (XRD),transmission electron microscopy (TEM),universal testing machine,and thermogravimetric analysis (TGA) were used to investigate the morphology,mechanical properties,and thermal stability of PA6/OMMT nanocomposites. With increasing contents of OMMT,the tensile strength,bending strength,bending modulus and heat distortion temperature of the PA6/OMMT nanocomposites increased. A tensile strength of 76 MPa,a bending modulus of 3.462 GPa,and a heat distortion temperature of 134 ℃ were obtained. The thermal stability of PA6 was also improved by OMMT,the temperature of 10 % weight loss reached 422 ℃,16 ℃ higher than that of neat PA6.