Abstract:The preparation of precursor sol is the first and crucial step in fabricating oxide fibers by the sol–gel method. In this study, different aluminum-silica sols were prepared by adjusting the alumina and silica source mixing procedure using aluminum carboxylate sol and tetraethoxysilane (TEOS) as the aluminum source and silicon source, respectively. Continuous alumina-mullite precursor fibers were obtained by dry spinning and the effects of alumina and silica source mixing procedure on the phase transition and microstructure evolution of alumina-mullite composite fibers were investigated. The results showed that the mullite formation temperature in the fibers obtained by adding TEOS during the preparation of aluminum carboxylate sol was about 1300 °C, while it was 800 °C in the fibers obtained by mixing aluminum carboxylate sol and TEOS. In addition, the grain size of the fibers obtained by adding TEOS during the preparation of aluminum carboxylate sol was significantly smaller than that obtained by mixing aluminum carboxylate sol and TEOS. The mechanism of this difference was that the aluminum-silica sol obtained by adding TEOS during the preparation of aluminum carboxylate sol was a diphasic sol, while the aluminum-silica sol obtained by adding TEOS in the prepared aluminum carboxylate sol was a monophasic sol.Graphical Abstract

Synthesis and Characterisation of Alumina Fibres Using Organic/Inorganic Composite Sol

Synthesis and Characterization of Polyvinyl Butyral–al(no 3 ) 3 Composite Sol Used for Alumina Based Fibers

Synthesis and characterization of sol-gel derived continuous spinning alumina based fibers with silica nano-powders

Synthesis and characterization of sol–gel alumina nanofibers

Synthesis and characterization of carbon nanofiber/alumina composite by extrusion casting

Insights into the pore-forming effect of polyvinyl butyral (PVB) as the polymer template to synthesize mesoporous alumina nanofibers via electrospinning

FABRICATION OF YTTRIUM ALUMINUM GARNET NANOFIBERS BY AN ELECTROSPINNING TECHNIQUE

Preparation and Characterization of Alumina Nanofibers by Gas-Solid Reaction Method

Preparation and mechanical performance of ductile Csf/Al2O3-BN composites, Part 1: Effects of fiber length and sintering temperature

Facile Electrospinning Preparation of Y3Al5O12 Nanobelts

Preparation and Characterization of Alumina-coated Hollow Quartz Fiber Reinforced Al2O3-SiO2 Aerogel Composite

Fabrication and Thermal Stability of Continuous Carbon Fiber Reinforced Alumina Matrix Composites via Sol–Gel Process

Mullite Fibres Prepared by Sol–gel Method Using Polyvinyl Butyral

Synthesis and Characterization of Rich Silica Mullite Fibers by Sol–Gel Method Using Aluminum Lactate and Silica Sol

Effect of formic-acid-to-acetic-acid ratio on the structure and spinnability of aqueous aluminium sol of alumina fibre

Fabrication of 6061 aluminium alloy/Al18B4O33(w) composite by using sol-gel alumina binder

Effect of Alumina Fiber Content on Pore Structure and Properties of Porous Ceramics

Mechanism of synthesizing Al2O3/Fe-Al composites with nano Al2O3 fibers by in-situ process

Effects of Alumina Sols on the Sintering of Α-Alumina Ceramics

Effect of the alumina and silica source mixing procedure on the microstructural evolution of alumina-mullite composite fibers prepared by sol–gel method

Preparation and Mechanical Property of Alumina Fibers Reinforced Thin Architectural Ceramic Plate