Abstract:In this study, a novel sol-gel method is used to synthesize amorphous silica-alumina materials with a narrow mesoporous distribution and various Si/Al molar ratios without using any templates and pore-regulating agents. During the preparation procedure, only inexpensive inorganic salts were used as raw materials, instead of expensive and harmful alkoxides. The precursor sol was dried at room temperature in a vacuum box kept at 60 mmHg until it began to form the gel. The results of a nitrogen sorption experiment indicate that the synthesized materials with different Si/Al molar ratios have similar mesoporous distributions (within 2-12 nm). Moreover, it was found that the material's pore size distribution remains at a similar value during the heat treatment from room temperature to 550 degreesC. On the basis of the nitrogen sorption, TEM, and AFM characterization results, a formation mechanism of mesopores which accounts for the experimental data is also suggested. This suggested mechanism involves rearrangement of the primary particles during the drying process to form the precursors of the similarly sized mesopores. The synthesized materials were characterized by XRD, thermal analysis (TG/DTA), Al-27 and Si-29 MAS NMR spectroscopy, SEM, TEM, and AFM. The results of Al-27 and 29Si MAS NMR indicate that the distribution of silicon and aluminum in the synthesized materials is more uniform and homogeneous than that in the mixed oxides prepared via the traditional sol-gel method even at high alumina contents. The type and density of the acid sites were studied using pyridine adsorption-desorption FTIR spectroscopy. It was shown that the acidity of the synthesized materials is higher than that of the silica-alumina materials prepared by conventional methods.

Synthesis and characterization of sol-gel derived continuous spinning alumina based fibers with silica nano-powders

Preparation of Continuous Alumina Fiber with Nano Grains by the Addition of Iron Sol

Effects of SiO2 Addition on Phase Transition and Microstructure Evolution of Alumina Fibers Prepared Using the Sol-Gel Method

Preparation and Properties of Nano-Silica/Calcium Alginate Blend Fibers

Synthesis and characterization of sol–gel alumina nanofibers

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics

Effect of the alumina and silica source mixing procedure on the microstructural evolution of alumina-mullite composite fibers prepared by sol–gel method

Polycrystalline Nanograin Formation in Uniform-Sized Silicon Carbide Fibers Derived from Aluminum-Containing Polycarbosilane

Poly(Methyl Methacrylate)/Silica Nanocomposite Fibers by Electrospinning

Synthesis and Characterization of Electrospun Mullite Nanofibers

Effect of silica sol on phase transition of alumina-mullite fibers

Structural Characterization of Mesoporous Silica Nanofibers Synthesized Within Porous Alumina Membranes

Research progress of ultrafine alumina fiber prepared by sol-gel method: A review

Effect Of Silica Sol On The Properties Of Alumina-Based Duplex Ceramic Cores

Sol-gel Preparation of Ag-silica Nanocomposite with High Electrical Conductivity

Preparation and Characterization of Alumina-coated Hollow Quartz Fiber Reinforced Al2O3-SiO2 Aerogel Composite

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

Preparation of high-strength alumina-zirconia fibers by the sol-gel method combined with two-step sintering processes

Effect of formic-acid-to-acetic-acid ratio on the structure and spinnability of aqueous aluminium sol of alumina fibre

Preparation and Characterization of Alumina Nanofibers by Gas-Solid Reaction Method

Alumina Ceramic Nanofibers: An Overview of the Spinning Gel Preparation, Manufacturing Process, and Application