Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

Synthesis and characterization of sol–gel alumina nanofibers

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Preparation and Characterization of Alumina Nanofibers by Gas-Solid Reaction Method

A Novel Sol–gel Synthetic Route to Alumina Nanofibers Via Aluminum Nitrate and Hexamethylenetetramine

Synthesis of Aluminium Borate Nanowires by Sol–gel Method

The Microstructure, Morphology, and Mechanical Properties of Sol-Gel-derived Amorphous Aluminum Oxide Films

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

Microstructures of Nanosized Alumina Powders Synthesized by Sol-Gel Method

PREPARATION AND CHARACTERIZATION OF ALUMINA NANOCRYSTALLINE POWDER BY COMPLEXING SOL-GEL METHOD

Preparation of Alumina Aerogel via Supercritical Method

Synthesis and structural characterization of alumina nanoparticles

Synthesis of γ-alumina via precipitation in ethanol

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

Preparation and Crystallization of Si-Al Gel

Alumina Ceramic Nanofibers: An Overview of the Spinning Gel Preparation, Manufacturing Process, and Application

Synthesis of monolithic aerogel-like alumina via the accumulation of mesoporous hollow microspheres

Effects of SiO2 Addition on Phase Transition and Microstructure Evolution of Alumina Fibers Prepared Using the Sol-Gel Method

Preparation and Characterization of Alumina-coated Hollow Quartz Fiber Reinforced Al2O3-SiO2 Aerogel Composite

Synthesis of Alumina Aerogels by Ambient Drying Method and Control of Their Structures

Preparation of Continuous Alumina Fiber with Nano Grains by the Addition of Iron Sol

Chemical and Structural Characterization of Amorphous and Crystalline Alumina Obtained by Alternative Sol–Gel Preparation Routes