Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Thermal and morphological study of Al2O3 nanofibers derived from boehmite precursor

Pore structure of aluminas derived from the alkyl derivatives of boehmite

Synthesis, Characterization and Catalytic Applications of Mesoporous Γ-Alumina from Boehmite Sol

Sol-Gel Synthesis of Alumina Using Inorganic Salt Precursor

Surface and pore structure of alumina derived from xerogel/aerogel

Synthesis and structural characterization of alumina nanoparticles

Synthesis and characterization of sol–gel alumina nanofibers

Study of Gamma Alumina Synthesis – Analysis of the Specific Surface Area

Porosity evaluation and positron annihilation study of mesoporous aluminum oxy-hydroxide ceramics

New sol-gel route using inorganic salt for synthesizing Al2O3 nanopowders

Optical and structural properties of spherical-shaped boehmite and γ-alumina nanoparticles by ultrasonic-assisted hydrothermal method: the effects of synthesis route, calcination, and precursor concentration

Synthesis of Al2O3 nanopowders using inorganic salt and its physical chemistry

Clean Synthesis of Hierarchically Structured Boehmite and Γ-Alumina with a Flower-Like Morphology

Preparation of Pseudo-Boehmite and Gamma-Al2o3 by Polyaluminum Chloride Ii -Surfactant Influences

Facile synthesis of nano-crystalline alpha-alumina at low temperature via an absolute ethanol sol-gel strategy

Hydrothermal stability of gamma-Al 2 O 3 supports varied with crystal plane orientation of pseudo-boehmite precursor

Tailored mesoporous alumina prepared from different aluminum alkoxide precursors

Quantitative Relationship Between the Density and Structural Unit of Alpha Alumina Prepared from Gibbsite and Boehmite

EFFECT OF NH4HCO3 ON PORE STRUCTURE OF ALUMINA