Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

Surface and pore structure of alumina derived from xerogel/aerogel

Pore structure of aluminas derived from the alkyl derivatives of boehmite

Sol-Gel Synthesis of Alumina Using Inorganic Salt Precursor

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

Synthesis and Thermal Behavior of High-Surface-Area Monolithic Alumina Aerogels

Preparation of Alumina Aerogel via Supercritical Method

Synthesis of High-Surface-Area Alumina Aerogels without the Use of Alkoxide Precursors

Synthesis of Alumina Aerogels by Ambient Drying Method and Control of Their Structures

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Synthesis of alumina aerogels from AlCl 3 ·6H 2 O with an aid of acetoacetic-grafted polyvinyl alcohol

Preparation and characterization of monolithic alumina aerogels

The Synthesis and Characterization of SiO_2-Al_2O_3 Xerogels

Synthesis and structural characterization of SiO2-Al 2O3 xerogels

The Microstructure, Morphology, and Mechanical Properties of Sol-Gel-derived Amorphous Aluminum Oxide Films

Al2O3 XEROGELS SYNTHESIZED BY INORGANIC SALT AND ORGANIC ALKOXIDE

Fabrication and Thermal Stability of La2O3 Doped Alumina Aerogel

Synthesis and Structural Characterization of SiO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub> Xerogels

Preparation of Pseudo-Boehmite and Gamma-Al2o3 by Polyaluminum Chloride Ii -Surfactant Influences

Chemical and Structural Characterization of Amorphous and Crystalline Alumina Obtained by Alternative Sol–Gel Preparation Routes

Fabrication of Hydrophobic Alumina Aerogel Monoliths by Surface Modification and Ambient Pressure Drying