Preparation of pseudo-boehmite via carbonation of sodium aluminate lixivium extracted from coal fly ash
Pengxu Cao,Dexi Gao,Jun Luo,Xinran Li,Lang Xing,Hao Jiang,Guanghui Li
DOI: https://doi.org/10.1016/j.micromeso.2023.112933
IF: 5.876
2023-12-08
Microporous and Mesoporous Materials
Abstract:The hydrothermal process was employed to extract alumina from coal fly ash, resulting in the production of sodium aluminate lixivium. The lixivium exhibited a low concentration of Na 2 O and Al 2 O 3 , which was subjected to carbonation to synthesize pseudo-boehmite in this study. During carbonation, the pH of the lixivium was decreased as CO 2 aeration, resulting in the formation of amorphous aluminum hydroxide, which subsequently transformed into pseudo-boehmite as the solution pH reached 10.0–10.5. Further decrease in solution pH below 9.5 caused the conversion of pseudo-boehmite into dawsonite. Monophase pseudo-boehmite was prepared from the lixivium after carbonation at 80–100 °C for 30–120 min with the final solution pH of 10.0–10.5. The resulting pseudo-boehmite exhibited a fibrous morphology and formed porous aggregations, which displayed a BET specific surface area of 445.48 m 2 /g, a cumulative pore volume of 0.76 cm 3 /g, with the majority of pores falling within the mesopore range of 2–50 nm. The pseudo-boehmite would dehydrate and transform into γ-Al 2 O 3 while maintaining its original morphology after calcination at 450–700 °C, making the product promisingly use as a precursor for preparing mesopore γ-Al 2 O 3 of widespread applications in industrial catalysis.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology, applied