Study of Gamma Alumina Synthesis – Analysis of the Specific Surface Area

Antonio Hortencio Munhoz Jr.,H. de Paiva,L. Figueiredo de Miranda,E.C. de Oliveira,Raphael Cons Andrades,R.R. Ribeiro
DOI: https://doi.org/10.4028/www.scientific.net/ast.87.54
2014-10-31
Abstract:Different samples of pseudoboehmite (PB) were synthesized through the sol-gel process, using aluminum nitrate as precursor. The influence of variables on the synthesis and calcinations of the PB on the specific area of the obtained gamma-Alumina were studied. The variables were the ageing temperature (25 and 130 o C), addition or not of polyvinyl alcohol to the precursor solution and the ageing time of the PB. The pH adjustment of the precursor solution was made by using ammonium carbonate. The products, which were obtained on different conditions, were then characterized by x-ray diffraction, specific area measurements through the BET process, and by thermal analysis (DTA and TG). After characterization, the synthesis products were calcined at 500°C; during this process the gamma-Alumina transformation was observed. The calcination products were characterized by the same methods (x-ray diffraction, BET, DTA and TG) and the desorption-absorption curves were obtained as well, in order to measure the pore volume of the samples. Finally, the results were analyzed through an experimental factorial planning, which showed that high specific surface area gamma-Al 2 O 3 (around 330m2/g) can be obtained through this process.
What problem does this paper attempt to address?