Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

Sol-Gel Synthesis of Transparent Alumina Gel and Pure Gamma Alumina by Urea Hydrolysis of Aluminum Nitrate

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Synthesis of Gamma-Alumina Nanopowders Using Waste Metal Aluminum and Stability Surfactants

Facile synthesis of nano-crystalline alpha-alumina at low temperature via an absolute ethanol sol-gel strategy

Synthesis of γ-alumina via precipitation in ethanol

The Microstructure, Morphology, and Mechanical Properties of Sol-Gel-derived Amorphous Aluminum Oxide Films

Preparation and Optical Properties of Transparent Alumina Film by the Sol-gel Method

Study of Gamma Alumina Synthesis – Analysis of the Specific Surface Area

Chemical and Structural Characterization of Amorphous and Crystalline Alumina Obtained by Alternative Sol–Gel Preparation Routes

Preparation of Alumina Ultrafine Powders Through Acrylamide, Starch and Glutaric Dialdehyde Mediated Sol–gel Method

Role of Ph, Organic Additive, and Chelating Agent in Gel Synthesis and Fluorescent Properties of Porous Monolithic Alumina

A Novel Synthesis Route of Mesoporous γ-Alumina from Polyoxohydroxide Aluminum

Synthesis of alumina aerogels from AlCl 3 ·6H 2 O with an aid of acetoacetic-grafted polyvinyl alcohol

The hydrolysis process of γ-AlON powder and preparation of highly transparent ceramics with aqueous gel-casting

Synthesis and sintering behavior of a nanocrystalline α-alumina powder

Ultrasonic Synthesis of Silica−Alumina Nanomaterials with Controlled Mesopore Distribution Without Using Surfactants

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

Ultrasound As a Tool to Synthesize Nano-Sized Silica–Alumina Catalysts with Controlled Mesoporous Distribution by a Novel Sol–Gel Process

Sol–gel synthesis, characterization and catalytic activity of γ-alumina with bimodal mesopore distribution

Synthesis and characterization of sol–gel alumina nanofibers