Abstract:Highly efficient and stable catalysts are among the key factors in industrial ethanol dehydration to ethylene. Among the widely studied catalysts, alumina is the most suitable for industrial application. In this study, novel gamma alumina was synthesized by solvent protection and a hydrothermal procedure. HRTEM, XRD, FT-IR, NH3-TPD, H-D exchange, and 29Si MAS NMR were employed to compare the difference in physicochemical properties between the novel gamma alumina and commercial alumina. Characterization results show that the as-synthesized novel gamma alumina mainly exposes the high-energy crystal plane (111) while the commercial alumina mainly exposes the thermostatically stable (110) crystal plane. The dominating (111) plane, according to the characterizations, endows the novel gamma alumina with a higher density of surface hydroxyl groups, higher acid content, and higher surface energy compared to the commercial alumina. The catalytic performance of the two catalysts for industrial ethanol dehydration to ethylene was studied. The novel (111) plane-exposed alumina showed a higher yield of ethylene than commercial alumina under the same reaction conditions. This could be related to the difference in atomic arrangement and the unsaturated aluminum coordination of different crystal planes. Stability testing under severe reaction conditions (450 °C, 1 MPa, 4 h−1) indicates that novel gamma alumina shows better stability (catalyst life cycle increased by 50%) and produces less acetaldehyde as a byproduct. The effects of steam treatment on the catalytic performance were further investigated. The surface acidity and the catalytic performance of novel gamma alumina present a volcanic curve with the increase in steam treatment temperature. Under the optimal water vapor treatment temperature of 650 °C, the conversion of ethanol and selectivity of ethylene were both higher than 99%.

Synthesis of γ-alumina via precipitation in ethanol

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Facile synthesis of nano-crystalline alpha-alumina at low temperature via an absolute ethanol sol-gel strategy

PREPARATION AND CHARACTERIZATION OF ALUMINA NANOCRYSTALLINE POWDER BY COMPLEXING SOL-GEL METHOD

Synthesis and sintering behavior of a nanocrystalline α-alumina powder

Gas-Liquid Interfacial Deposition Synthesis of Alumina with Large Mesopores

Synthesis and characterization of sol–gel alumina nanofibers

Synthesis of nano α-alumina powders using hydrothermal and precipitation routes: a comparative study

Preparation of micron-sized alumina powders from aluminium beverage can by means of sol-gel process

Synthesis of highly porous nanocrystalline alumina as a robust catalyst for dehydration of methanol to dimethyl ether

Synthesis of Gamma-Alumina Nanopowders Using Waste Metal Aluminum and Stability Surfactants

Preparation and Characterization of Nanocrystalline Gamma-Al2o3 by Sol-Gel Process

Size-controlled synthesis of nano α-alumina particles through the sol–gel method

Preparation of Alumina Aerogel via Supercritical Method

Preparation of High-Surface-Area Γ-Alumina by Assistance of Sucrose

Preparation of Near-Spherical α-Al2O3 Particles by Enhanced Precipitation of Gibbsite from Sodium Aluminate Solution Using Highly Dispersed Al2O3 as Seeds

Ethanol Dehydration to Ethylene over High-Energy Facets Exposed Gamma Alumina

Coprecipitation Synthesis of Large-Pore-Volume Γ-Alumina Nanofibers by Two Serial Membrane Dispersion Microreactors with a Circulating Continuous Phase

Sol-Gel Synthesis of Transparent Alumina Gel and Pure Gamma Alumina by Urea Hydrolysis of Aluminum Nitrate

Sol–gel synthesis, characterization and catalytic activity of γ-alumina with bimodal mesopore distribution

Preparation of Near-Spherical α-Al 2 O 3 Particles by Enhanced Precipitation of Gibbsite from Sodium Aluminate Solution Using Highly Dispersed Al 2 O 3 as Seeds