Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

Hydrothermal stability of gamma-Al 2 O 3 supports varied with crystal plane orientation of pseudo-boehmite precursor

Facile Preparation and Promising Hydrothermal Stability of Spherical γ-Alumina Support with High Specific Surface Area

Quantification of surface orientation effect on the thermal stability of γ-Al2O3 with different morphologies

Influence of preparation methods and additives on hydrothermal stability of γ-Al2O3

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

Preparation and performance of high thermal-stable alumina-substrate materials

Morphology Evolution in Hydrothermal Synthesis of Mesoporous Alumina

Preparation of Pseudo-Boehmite and Gamma-Al2o3 by Polyaluminum Chloride Ii -Surfactant Influences

Facile Synthesis of Hierarchical Flower-Like Γ-Alooh Films Via Hydrothermal Route on Quartz Surface

Preparation of High Thermal-Stabile Alumina by Reverse Microemulsion Method

Study of Gamma Alumina Synthesis – Analysis of the Specific Surface Area

Preparation and Property of Pseudoboehmite by Polyaluminum Cloride

Effects of synthetic conditions on the textural structure of pseudo-boehmite

INFLUENCE OF DRYING TEMPERATURE OF PSEUDO-BOEHMITE ON CRUSH STRENGTH OF Γ-Al2o3 SUPPORT

Preparation and properties of high-purity porous alumina support at low sintering temperature

Synthesis, Characterization and Catalytic Applications of Mesoporous Γ-Alumina from Boehmite Sol

Preparation of pseudo-boehmite via carbonation of sodium aluminate lixivium extracted from coal fly ash

A Facile Temperature-Controlled "Green" Method to Prepare Multi-kinds of High-Quality Alumina Hydrates via a Ga-In-Sn-Alloyed Aluminum-Water Interface Reaction.

Fabricating Mesoporous Silica-Modified Alumina with High Thermal Stability

Fabrication and Thermal Stability of La2O3 Doped Alumina Aerogel

Surface and pore structure of alumina derived from xerogel/aerogel