INFLUENCE OF DRYING TEMPERATURE OF PSEUDO-BOEHMITE ON CRUSH STRENGTH OF Γ-Al2o3 SUPPORT

杨清河,刘滨,聂红,石亚华,李大东

DOI: https://doi.org/10.3969/j.issn.1001-8719.2003.02.013

2003-01-01

Abstract:Crush strength is one of the most important variables of hydrotreating catalyst, which depends mainly upon that of its support. The influence of drying temperature of pseudo-boehmite on crush strength of γ -Al_2O_3 support was studied. Pseudo-boehmite was dried at temperature ranged from 60 to 110 ℃. It was found that drying temperature of pseudo-boehmite played an important role on crush strength of γ -Al_2O_3 support. When pseudo-boehmite was dried at 60 ℃, crush strength of γ -Al_2O_3 support, prepared from dried pseudo-boehmite, was 21.9 N/mm. Furthermore, the consistence of crush strength σ_ 11 X - was 11.6% (σ_ 11 X - is used to express consistence of crush strength. Lower value ofσ_ 11 X -, better consistence of crush strength). When pseudo-boehmite was dried at 90 ℃, the crush strength of γ -Al_2O_3 support was 20.8 N/mm and σ_ 11 X - was 24.9%. When pseudo-boehmite was dried at 110 ℃, the crush strength of γ -Al_2O_3 support was 12.4 N/mm, much lower than that dried at 60 ℃. At the same time it showed much less consistent, σ_ 11 X - was 32.2%. Influence of drying temperature of pseudo-boehmite on crush strength of γ -Al_2O_3 support was possibly related to some 'extro-water' bonded to the surface of particles of pseudo-boehmite through hydrogen bond, which was formed during production of pseudo-boehmite.