Abstract:Magnesium aluminate spinel (MgAl2O4) ceramics are high-performance and carbon-free materials widely used in both military and civilian fields. However, it is usually challenging to densify during the solid-state sintering process. The excellent properties of some rare earth oxides have been proved to promote the densification of MgAl2O4 spinel ceramics. But the mechanism of promoting sintering is not clear. In the present work, MgAl2O4 spinel ceramics have been successfully fabricated by co-doping CeO2 and La2O3 via a single-stage solid-state reaction sintering. The effects of addition amounts of CeO2 and La2O3 on phase compositions, microstructures, sintering characteristics, cold compressive strength, and thermal shock resistance of as-prepared MgAl2O4 spinel ceramics were systematically investigated. The results show that by co-doping CeO2 and La2O3 can increase the defect concentration due to the lattice distortion. This could promote the movement of Al3+ and Mg2+ at high temperature, which is beneficial to the formation of more secondary MgAl2O4 spinel. t-ZrO2 with more Ce4+ filling between spinel grains could prevent the growth of grains and promote the densification, besides the new-formed LaAlO3 that was mainly distributed along the grain boundary of the MgAl2O4 phase, both of which were favorable for the formation of dense microstructure of MgAl2O4 spinel materials. At the same time, the formation of more secondary MgAl2O4 spinel and sintering densification also improve the mechanical properties of spinel ceramics. La3+ will segregate to the spinel grain boundary, preventing grain boundary movement and absorbing the main crack's fracture energy. With 3 wt% CeO2 and 3 wt% La2O3 co-doping, the bulk density of the sample increased from 3.02 g∙cm−3 to 3.55 g∙cm−3; the apparent porosity decreased from 12.21% to 9.97%; the cold compressive strength increased from 172.88 MPa to 189.54 MPa; and the residual strength retention ratio after thermal shock increased from 84.92% to 89.15%.

Preparation and Characterization of Porous Mgal2o4 Spinel Ceramic Supports from Bauxite and Magnesite

Synthesis and Characterization of Porous Magnesium Aluminate Spinel by Hydrothermal Process

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Effect of different MgO/Al2O3 ratios on microstructural densification, sintering process and mechanical property of MgAl2O4 materials

Preparation and properties of MgAl2O4 spinel ceramics by double-doped CeO2 and La2O3

Preparation of High Purity Alumina Ceramic Supports at Low Temperature

Preparation and properties of porous MgO based ceramics from magnesite tailings and fused magnesia

A strategy for controlling microstructure and mechanical properties of microporous spinel (MgAl2O4) aggregates from magnesite and Al(OH)3

Novel Synthesis of High Surface Area MgAl2O4 Spinel As Catalyst Support

Characterization of Spinel Bubbles and Preparation and Properties of Lightweight Ceramics

Recycling bagasse and rice hulls ash as a pore‐forming agent in the fabrication of cordierite‐spinel porous ceramics

Mechanism of in-situ formation of spinel and its effect on the mechanical properties of Al2O3–C refractories

Preparation and properties of high-purity porous alumina support at low sintering temperature

Preparation and properties of porous ceramics from spodumene flotation tailings by low-temperature sintering

Effect of Magnesia-Alumina Spinel Precursor Sol on the Sintering Property of Fused Magnesia Refractory

Preparation and characterization of tubular porousα-Al_2O_3 ceramic membrane support

Influence of in situ formed spinel in bonding phase on mechanical properties and air permeability of magnesia–chrome porous purging materials

Preparation of Porous Ceramic Materials by Alumina Fiber Framework

Preparation and Characterization of Novel Nonstoichiometric Magnesium Aluminate Spinels

Fabrication and Characterization of Porous Cordierite Ceramics Prepared from Fly Ash and Natural Minerals