Abstract:Abundant availability of fly ash due to the combustion of coal in thermal power plants presents a major threat to rising environmental pollution. To preserve the environment, fly ash was explored as the starting material for cordierite synthesis. Cordierite ceramics are widely used in the production of microelectronic components, catalyst substrate material for internal combustion engine. Hence, this research was pursued to fabricate the cordierite in a cost effective manner using fly ash containing the major constituent’s silica (SiO2) and alumina (Al2O3). Cordierite synthesis is carried out using raw materials fly ash, magnesia and dopants such as ZrO2, CeO2 and TiO2 at different composition (5–20 wt%). The properties and the microstructure of prepared samples were evaluated using X-ray diffraction (XRD), thermogravimetric and differential thermal analysis (TG/DTA), and scanning electron microscopy. Their mechanical and thermal properties such as the hardness, the fracture toughness, the flexural strength and the thermal expansion coefficient (CTE) were studied and compared with their morphology. It was found that the hardness, the fracture toughness, and the flexural strength were improved on the addition of the dopant in the cordierite matrix. The cordierite-ZrO2 ceramics (CZr20) exhibited a Vickers hardness value of 7.04 GPa, the fracture toughness of 3.47 MPa m½, and flexural strength of 196.72 MPa. The results confirm the cordierite synthesized with fly ash along with dopants is found suitable for use as catalytic substrate materials with improved mechanical properties.

Fabrication and Characterization of Porous Cordierite Ceramics Prepared from Fly Ash and Natural Minerals

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

In-situ synthesis and properties of porous cordierite ceramics with adjustable pore structure

Formation and kinetics of porous cordierite from fly ash

Low-Temperature Preparation of Porous Cordierite Materials with Fly Ash and Magnesite

Fabrication and Properties of Porous Sic-Cordierite Ceramics

Phase Evolution and Properties of Porous Cordierite Ceramics Prepared by Cordierite Precursor Pastes Based on Supportless Stereolithography

Effect of Mineral Composition and Sintering Temperature on the Synthetic Cordierite

Synthesis of Porous Cordierite Using Rice Husk As Silica Source and Pore Forming Agent

Utilization of Sepiolite in the Synthesis of Porous Cordierite Ceramics

Characterization of cordierite-based glass-ceramics produced from fly ash

Fabrication of dense cordierite ceramic through reducing Al2O3 mole ratio

Fabrication and Properties of Cordierite–mullite Bonded Porous SiC Ceramics

Mechanism of Cordierite Formation Obtained by High Temperature Sintering Technique

Facile fabrication of cordierite-based porous ceramics with magnetic properties

A simple method for the preparation of cordierite ceramics with high strength and low thermal expansion coefficient

Preparation and characterization of porous anorthite ceramics from red mud and fly ash

Near Net Shape Fabrication of Porous Cordierite by Combination of Foam Gel‐casting and Freeze‐drying

Fly Ash Constituent-Silica and Alumina Role in the Synthesis and Characterization of Cordierite Based Ceramics

Preparation and characterization of cordierite powders by water-based sol-gel method

Formation, Conversion and Elimination of Intermediate Spinel Phase in MgO/kaolin Mixture Firing for Cordierite