Abstract:High-alumina fly ash microbeads and steel slag were used as main raw materials to synthesize feldspar porous ceramics via high-temperature solid phase sintering by adding pulverized coal as a pore-forming agent. The effects of the steel slag and pore-forming agent on the apparent porosity and flexural strength of porous ceramics were investigated. The phase composition and microstructure of porous ceramics were characterized using X-ray diffraction and scanning electron microscopy, and the results indicated that the added amount of steel slag was only related to the amount of liquid phase formed in porous ceramics. The higher the amount of steel slag added, the more the liquid phase formed. At the same sintering temperature, the higher the pore former content, the higher the porosity of the porous ceramics and the lower the bending strength. When porous ceramics were sintered at 1160 °C steel slag melted and fly ash microsphere structures were formed. When the porous ceramics were sintered at 1190 °C, the fly ash microsphere structure disappeared. After the internal liquid phase of the ceramic was formed, the lower the sintering temperature, the larger the porous ceramic structure factor, the more sensitive the flexural strength to changes in porosity and the higher the theoretical strength of ceramic densification. Moreover, as the sintering temperature decreased, the network structure formed during the reaction of fly ash microbeads with CaO greatly increased the flexural strength of fly ash ceramics. When the sintering temperature, sintering time and pore former content were 1170 °C, 120 min, and 10%, respectively, the obtained porous ceramics presented superior apparent porosity and flexural strength (49.21% and 12.88 MPa, respectively), and the main crystalline phase of porous ceramics was anorthite featuring pore size ranging from 5 to 50 μm.

Formation and kinetics of porous cordierite from fly ash

Fabrication and Characterization of Porous Cordierite Ceramics Prepared from Fly Ash and Natural Minerals

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Low-Temperature Preparation of Porous Cordierite Materials with Fly Ash and Magnesite

Preparation and characterization of the porous ceramics from fly ash

Fabrication and Properties of Porous Sic-Cordierite Ceramics

In-situ synthesis and properties of porous cordierite ceramics with adjustable pore structure

Fly Ash Constituent-Silica and Alumina Role in the Synthesis and Characterization of Cordierite Based Ceramics

Preparation of anorthite-based porous ceramics using high-alumina fly ash microbeads and steel slag

Cordierite-Based Ceramics from Coal Fly Ash for Thermal and Electrical Insulations

Sintering and Characterization of Flyash-Based Mullite with MgO Addition

Synthesis of Porous Cordierite Using Rice Husk As Silica Source and Pore Forming Agent

Sintering Kinetics of Porous Ceramics from Natural Diatomite

Characterization of cordierite-based glass-ceramics produced from fly ash

Reaction Sintering Kinetics of Mullite Ceramics Prepared from High Aluminum Fly Ash

Utilization of Sepiolite in the Synthesis of Porous Cordierite Ceramics

Phase Evolution and Properties of Porous Cordierite Ceramics Prepared by Cordierite Precursor Pastes Based on Supportless Stereolithography

Low-temperature preparation of porous cordierite-mullite ceramics using rice husk as silica source and pore-forming agent

Formation, Conversion and Elimination of Intermediate Spinel Phase in MgO/kaolin Mixture Firing for Cordierite

Preparation Of Porous Mullite Ceramics Using Fly Ash Cenosphere As A Pore-Forming Agent By Gelcasting Process

Preparation and characterization of porous anorthite ceramics from red mud and fly ash