Abstract:Low-temperature sintering of cordierite ceramic depends on the phase transformation into cordierite and the properties depend on its microstructure. In the present work, the effect of cerium on the phase transformation and microstructure of cordierite ceramics prepared by sol-gel method is studied by X-ray diffraction (XRD), differential thermal analysis (DTA) and scanning electron microscopy (SEM) in order to lower the sintering temperature and improve the properties of cordierite ceramic with the addition of cerium. It is observed that the cerium addition obviously lowers the crystallization temperature of α-cordierite while slightly raises that of μ-cordierite. The lowest temperature for μ → α cordierite transformation, which approaches the crystallization temperature of μ-cordierite, is achieved in the sample containing 4 wt% of cerium, implying a possibility to lower the sintering temperature of cordierite ceramics. The Ce-contained ceramics show a biphasic microstructure that is dependent on sintering temperature. Sintered below 1300°C, a cordierite-CeO 2 microstructure is present; while sintered at the temperature above 1300°C, appears a cordierite-glass microstructure, of which the amount of glass phase is limited to a small extent. Since the addition of 4 wt% cerium to this MgO-Al 2 O 3 -SiO 2 system substantially enhances the densification of cordierite ceramics and lowers the sintering temperature to the level of around 1000°C, it makes the ceramics suitable for such applications, where the low-temperature sintering is required, as the substrates for electronic circuit and the catalytic supports (with oxygen storage capacity) for cleaning of automotive exhaust emissions.

Low-temperature preparation of porous cordierite-mullite ceramics using rice husk as silica source and pore-forming agent

Influence of Nd2O3 on Porous Cordierite Prepared from Rice Husk

Synthesis of Porous Cordierite Using Rice Husk As Silica Source and Pore Forming Agent

Influence of La_2O_3 on Preparation and Performance of Porous Cordierite from Rice Husk

Low-Temperature Preparation of Porous Cordierite Materials with Fly Ash and Magnesite

Utilization of Sepiolite in the Synthesis of Porous Cordierite Ceramics

Fabrication and Characterization of Porous Cordierite Ceramics Prepared from Fly Ash and Natural Minerals

Effect of Mineral Composition and Sintering Temperature on the Synthetic Cordierite

Fabrication Of Sio2 Porous Ceramics From Rice Husk Ash

In-situ synthesis and properties of porous cordierite ceramics with adjustable pore structure

A simple method for the preparation of cordierite ceramics with high strength and low thermal expansion coefficient

INFLUENCE OF Al2O3 ON PREPARING POROUS SILICON NITRIDE BASED CERAMIC FROM RICE HUSK

Low-temperature Densification and Mechanical Properties of Monolithic Mullite Ceramic

Fabrication of SiO<sub>2</sub> Porous Ceramics from Rice Husk Ash

Preparation of Porous Mullite Ceramics with Low Thermal Conductivity

A Simple and Efficient Way to Prepare Porous Mullite Matrix Ceramics Via Directly Sintering SiO2-Al2O3 Microspheres

Synthesis of Cordierite Powders by Low Temperature Combustion Method

Effect of Cerium Addition on Phase Transformation and Microstructure of Cordierite Ceramics Prepared by Sol-Gel Method

Low-temperature Synthesis of Highly Porous Whisker-Structured Mullite Ceramic from Kaolin

Fabrication and Properties of Cordierite–mullite Bonded Porous SiC Ceramics

Recycling bagasse and rice hulls ash as a pore‐forming agent in the fabrication of cordierite‐spinel porous ceramics