Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

EFFECT OF NH4HCO3 ON PORE STRUCTURE OF ALUMINA

The Effect of CaO Content on Sorption Performance of Nano CaO Based CO2 Adsorbent

Effect of Type and Content of Pore-forming Agents on Properties of Porous Alumina Membrane Support

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Properties of a Nano CaO/Al<sub>2</sub>O<sub>3</sub>CO<sub>2</sub>Sorbent

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Preparation of pseudo-boehmite and γ-Al2O3 support by neutralization of NaAlO2 with CO2

Studies on preparation of Pseudo-boehmite from neutralization of NaAlO2 aqueous solution by co2

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

Tuning the structure of alumina

Preparation of Pseudo-boehmite and Γ-Al2o3 Support by Neutralization of NaAlO2 Solution with CO2

Effect of Pore Size Distribution of Carbon‐Covered Alumina on the Preparation of Submicrometer Α‐alumina Powders

Gas-Liquid Interfacial Deposition Synthesis of Alumina with Large Mesopores

Effect of NH4Cl on the a phase transformation of Al2O3 derived from ammonium aluminum carbonate hydroxide

Effect of Alumina Structure on Catalytic Ozonation Activity

Synthesis, Characterization and Catalytic Applications of Mesoporous Γ-Alumina from Boehmite Sol

Effects of aluminum on micro-sized pore structure of porous MoAlB ceramics fabricated via reactive synthesis

Effect of Aqueous Ammonia Medium and Fluorine Treatment on Properties of Alumina-Pillared Clays

Pore structure of aluminas derived from the alkyl derivatives of boehmite

Preparation of new porous catalytic material Al2O3-NaY through hydrolysis of aluminum isopropoxide

Preparation of pseudo-boehmite via carbonation of sodium aluminate lixivium extracted from coal fly ash