Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

Microstructures of Nanosized Alumina Powders Synthesized by Sol-Gel Method

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

PREPARATION AND CHARACTERIZATION OF ALUMINA NANOCRYSTALLINE POWDER BY COMPLEXING SOL-GEL METHOD

Synthesis of Aluminium Borate Nanowires by Sol–gel Method

The Microstructure, Morphology, and Mechanical Properties of Sol-Gel-derived Amorphous Aluminum Oxide Films

Tuning the structure of alumina

Synthesis and sintering behavior of a nanocrystalline α-alumina powder

Synthesis and characterization of sol–gel alumina nanofibers

Preparation of Alumina Aerogel via Supercritical Method

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

A Novel Sol–gel Synthetic Route to Alumina Nanofibers Via Aluminum Nitrate and Hexamethylenetetramine

Synthesis and structural characterization of alumina nanoparticles

Effects of SiO2 Addition on Phase Transition and Microstructure Evolution of Alumina Fibers Prepared Using the Sol-Gel Method

Sol-Gel Synthesis of Nano-Sized Silica-Alumina Mesoporous Molecular Sieves with Bimodal Pore Structure

Preparation and Crystallization of Si-Al Gel

Al2O3 Ceramics with Well-Oriented and Hexagonally Ordered Pores: the Formation of Microstructures and the Control of Properties

Structural Characterization of Mesoporous Silica Nanofibers Synthesized Within Porous Alumina Membranes

Ultrasonic Synthesis of Silica−Alumina Nanomaterials with Controlled Mesopore Distribution Without Using Surfactants

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

Size-controlled synthesis of nano α-alumina particles through the sol–gel method

Structure and phase changes of alumina produced by flame hydrolysis