Abstract:In this study, a novel sol-gel method is used to synthesize amorphous silica-alumina materials with a narrow mesoporous distribution and various Si/Al molar ratios without using any templates and pore-regulating agents. During the preparation procedure, only inexpensive inorganic salts were used as raw materials, instead of expensive and harmful alkoxides. The precursor sol was dried at room temperature in a vacuum box kept at 60 mmHg until it began to form the gel. The results of a nitrogen sorption experiment indicate that the synthesized materials with different Si/Al molar ratios have similar mesoporous distributions (within 2-12 nm). Moreover, it was found that the material's pore size distribution remains at a similar value during the heat treatment from room temperature to 550 degreesC. On the basis of the nitrogen sorption, TEM, and AFM characterization results, a formation mechanism of mesopores which accounts for the experimental data is also suggested. This suggested mechanism involves rearrangement of the primary particles during the drying process to form the precursors of the similarly sized mesopores. The synthesized materials were characterized by XRD, thermal analysis (TG/DTA), Al-27 and Si-29 MAS NMR spectroscopy, SEM, TEM, and AFM. The results of Al-27 and 29Si MAS NMR indicate that the distribution of silicon and aluminum in the synthesized materials is more uniform and homogeneous than that in the mixed oxides prepared via the traditional sol-gel method even at high alumina contents. The type and density of the acid sites were studied using pyridine adsorption-desorption FTIR spectroscopy. It was shown that the acidity of the synthesized materials is higher than that of the silica-alumina materials prepared by conventional methods.

A Novel Sol–gel Synthetic Route to Alumina Nanofibers Via Aluminum Nitrate and Hexamethylenetetramine

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Synthesis and characterization of sol–gel alumina nanofibers

Preparation of Alumina Nanofibers by Oxidation of Amalgam

A new route to synthesis of γ-alumina nanorods

The Microstructure, Morphology, and Mechanical Properties of Sol-Gel-derived Amorphous Aluminum Oxide Films

Preparation and Characterization of Alumina Nanofibers by Gas-Solid Reaction Method

Synthesis of Aluminium Borate Nanowires by Sol–gel Method

Facile synthesis of monodisperse aluminum nitride microspheres

Preparation of Alumina Ultrafine Powders Through Acrylamide, Starch and Glutaric Dialdehyde Mediated Sol–gel Method

Microstructures of Nanosized Alumina Powders Synthesized by Sol-Gel Method

Facile synthesis of nano-crystalline alpha-alumina at low temperature via an absolute ethanol sol-gel strategy

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

Hydrothermal synthesis of boehmite nanorods from alumina sols

AlN Nanoparticles Prepared Through a Gelation-Polymerization Process

Ultrasonic Synthesis of Silica−Alumina Nanomaterials with Controlled Mesopore Distribution Without Using Surfactants

Synthesis and characterization of sol-gel derived continuous spinning alumina based fibers with silica nano-powders

Preparation of Continuous Alumina Fiber with Nano Grains by the Addition of Iron Sol

Hydrothermal routes to various controllable morphologies of nanostructural lithium aluminate

Synthesis of aluminum nitride fibres from aluminum silicate fibres by carbothermal reduction method

Synthesis of nano α-alumina powders using hydrothermal and precipitation routes: a comparative study