Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

A new route to synthesis of γ-alumina nanorods

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Hydrothermal synthesis of boehmite nanorods from alumina sols

Synthesis and Characterization of Gibbsite Nanostructures

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

One-pot Template-Free Synthesis of Mesoporous Boehmite Core–shell and Hollow Spheres by a Simple Solvothermal Route

Hydrothermal synthesis of microscale boehmite and gamma nanoleaves alumina

Hydrothermal Preparation Of Boehmite Nanorods By Selective Adsorption Of Sulfate

A Novel Sol–gel Synthetic Route to Alumina Nanofibers Via Aluminum Nitrate and Hexamethylenetetramine

H2SO4-assisted hydrothermal preparation of γ-AlOOH nanorods

Facile Synthesis of Hierarchical Flower-Like Γ-Alooh Films Via Hydrothermal Route on Quartz Surface

Synthesis of Aluminium Borate Nanowires by Sol–gel Method

Catalysed Growth of Novel Aluminium Oxide Nanorods

Hierarchical nanoarchitectonics of boehmite: The preparation of three-dimensional flower-like via hydrothermal method without surfactants

Hydrothermal synthesis and characterization of core/shell ALOOH microspheres

Size and Morphology Controlled Synthesis of Boehmite Nanoplates and Crystal Growth Mechanisms

Synthesis, Characterization and Catalytic Applications of Mesoporous Γ-Alumina from Boehmite Sol

Preparation of high pore volume γ-Al2O3 nanorods via “gibbsite-AACH” precursor route in a membrane dispersion microreactor

Hydrothermal routes to various controllable morphologies of nanostructural lithium aluminate

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

Synthesis,Structure and Growth Mechanism of Aluminum Borate Nanorods