Fabrication of 6061 aluminium alloy/Al18B4O33(w) composite by using sol-gel alumina binder

Dongyan Ding,Jiannong Wang

DOI: https://doi.org/10.1179/026708301101510942

IF: 1.8

2013-01-01

Materials Science and Technology

Abstract:For fabrication of aluminium borate whisker (Al18B4O33(w)) reinforced 6061 aluminium alloy composites, a sol-gel alumina binder instead of conventional silica binder was used for preparing the whisker preforms of the squeeze cast composites. The results show that a sound whisker preform and a uniform composite can be made by this method. Unlike the reactive silica binder, the sol-gel alumina binder is rather stable throughout the entire high temperature fabrication process. Under appropriate conditions, the sol-gel alumina binder can also serve as a thermal barrier for minimising interfacial reactions between aluminium borate whiskers and the matrix alloy. With a binder concentration of 0.6 mol L-1, the ultimate tensile strength of the composite is as high as 277.6 MPa at room temperature and moderate at elevated temperatures. The tensile fracture of the alumina bound composite shows a mixed mode of dimple fracture and interface debonding. (C) 2001 IoM Communications Ltd.