Abstract:diameter of 0.5‐1 µm and length of 10‐30 µm. The aluminum matrix composite reinforced by both β-eucryptite particles and aluminum borate whiskers ((Euc + ABO)/AA6061) was fabricated by a squeeze casting technique. The total volume fraction of β-eucryptite particles and aluminum borate whiskers was 40%, and the volume ratio between β-eucryptite and aluminum borate was 2:1. The pressure for squeeze casting was 30 MPa. The casting temperature of AA6061 was 800 ◦ C and the die temperature was about 520 ◦ C. In order to compare the properties of (Euc + ABO)/AA6061 with those of other materials, the composites reinforced by aluminum borate whiskers and silicon carbide whiskers were also fabricated on the above condition. The volume fractions of the reinforcements in the two composites were 25%. Tensile specimens were cut from the squeezing composite ingot. The tensile test was carried out on a CSS4400 tensile machine. The dimension of the specimens for the CTE measurement is φ 5m m× 18 mm. The CTE curve was measured on a Netzch DIL 401C Dilatometer with a heating rate of 8 ◦ C/min. The microstructure was examined by an Olympas PMG3 type optical microscope (OM). The OM photograph of the (Euc + ABO)/AA6061 composite is shown in Fig. 1. It can be seen that the distribution of β-eucryptite particles and aluminum borate whiskers in the composite are random and homogeneous. The comparison of the tensile strengths of the various materials is given in Fig. 2, which includes (Euc + ABO)/AA6061, AA6061, AA6061 matrix composites

Fabrication and characteristic of Al-based hybrid composite reinforced with tungsten oxide particle and aluminum borate whisker by squeeze casting

The properties and microstructure of hybrid composites reinforced with WO3 particles and Al18B4O33 whiskers by squeeze casting

MMCs with Controlled Non-Uniform Distribution of Submicrometre Al2O3particles in 6061 Aluminium Alloy Matrix

Fabrication and Characteristics of (abow Plus Sicp)/6061al Composite by Semi-Solid Mechanical Stirring Technique

An Aluminum Borate Whisker-Reinforced Aluminum Matrix Composite with High Plasticity

Microstructure and Mechanical Properties of ABOw and Nickel-Coated MWCNTs Reinforced 2024al Hybrid Composite Fabricated by Squeeze Casting

Preparation of Novel Aluminum Hybrid Composite Containing Aluminum Borate Whiskers and Carbon Nanotubes

High-strength and High-Modulus Al18B4O33W/GWZ1031K Magnesium Matrix Composite Prepared by Squeeze Casting

Mechanical properties of ABOw+MWNTs/Al hybrid composites made by squeeze cast technique

Preparation and Characteristics of Al Matrix Composites Reinforced with ZnWO4 Coated (wo3p + ABOw) Hybrid Reinforcements

Fabrication and Characteristics of in Situ Al12w Particles Reinforced Aluminum Matrix Composites by Reaction Sintering

Fabrication and mechanical properties of α-Al2O3 whisker reinforced cu-graphite matrix composites

A study on an aluminum matrix composite reinforced by both β-eucryptite particle and aluminum borate whisker

Interfacial microstructure and tensile properties of 6061Al matrix composite reinforced with ZnAl2O4-coated Al18B4O33 whiskers

Fabrication and Evaluation of Al-based Hybrid Composites Reinforced with SiC Whiskers and SiC Nanoparticles

Fabrication of Al-based hybrid composites reinforced with SiC whiskers and SiC nanoparticles by squeeze casting

Fabrication and strengthening mechanism of dual-phased and bimodal-sized (Si3N4p + TiB2p)/6061Al hybrid composite

Microstructures and Tensile Properties of Hot-Extruded Composite Bi 2 O 3 -Coated ABOw/Al Composite

Aluminum matrix composite with eucryptite particle and aluminum borate whisker

Effects of ZnO Coating on the Wettability and Tensile Properties of Aluminum Borate Whisker-Reinforced Aluminum Composite

New aluminum matrix composite with much lower coefficient of thermal expansion and higher strength