Abstract:A reciprocating extrusion process was developed to consolidate 6061-Al 2 O 3 p composites from mixed powders. The 6061 alloy powder was first dehydrated in a vacuum chamber at 450 °C and then mixed with 12.5 µm Al 2 O 3 powder in various volume fractions: 0, 5, 10, 20, and 30 pct. The mixed powders were hot pressed at 300 °C under a pressure of 300 MPa and finally extruded reciprocatingly 14 times at 460 °C. The results show that the composites were fully densified, with no sign of pores or oxide layers observable in the optical microscope. The Al 2 O 3 particles were distributed uniformly in the matrix. As compared with 6061 alloys, the composites demonstrated a smaller precipitation hardening and elongation, but exhibited a higher Young’s modulus and a larger work hardening capacity. The degradation of precipitation hardening was due to the loss of Mg, which reacts with Al 2 O 3 to form MgAl 2 O 4 . The large work-hardening capacity is attributable to the incompatibility between Al 2 O 3 and the matrix, which possibly generates more dislocations to harden the matrix. The composites had much higher friction coefficients and greater wear resistances than the 6061 alloy against steel disc surface. The friction coefficient of the 6061-30 vol pct Al 2 O 3 p composite was double that of the 6061 alloy and the wear resistance was 100-fold. As compared with similar composites reported previously, these composites possessed much higher elongation at the same strength level. A 30 vol pct Al 2 O 3 p still displayed an elongation of 9.8 pct in the T6 condition. All of these improvements are attributed to the merits, including full densification of the bulk, uniform dispersion of the Al 2 O 3 particles in the matrix, and strong binding between the Al 2 O 3 particles and the matrix resulting from reciprocating extrusion.

High Strength Al(2)O(3)P/6061 Al Composites: Effect Of Particles, Subgrains And Precipitates

High strength Al<SUB>2</SUB>O<SUB>3p</SUB>/6061 Al composites: effect of particles, subgrains and precipitates

MMCs with Controlled Non-Uniform Distribution of Submicrometre Al2O3particles in 6061 Aluminium Alloy Matrix

High Strength Al–Al2O3p Composites: Optimization of Extrusion Parameters

FLEXURAL STRENGTH OF IN-SITU REACTION PROCESSED Al2O3-Al3Ti-Al COMPOSITES

In situ (Al3Zrp+Al2O3np)/2024Al metal matrix composite with controlled reinforcement architecture fabricated by reaction hot pressing

Microstructures and Mechanical Properties of Engineered Short Fibre Reinforced Aluminium Matrix Composites

Study of 6061-Al2o3p Composites Produced by Reciprocating Extrusion

Effect of coating Al2O3 reinforcing particles on the interface and mechanical properties of 6061 alloy aluminium matrix composites

Achieving ultra-high strength in Be/Al composites by self-exhaust pressure infiltration and hot extrusion process

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF Y2O3 MODIFIED-Al2O3 PARTICLE /6061Al COMPOSITES

Fabrication and strengthening mechanism of dual-phased and bimodal-sized (Si3N4p + TiB2p)/6061Al hybrid composite

Microstructure and Mechanical Properties of Al/Al4C3/Al2O3 Composite

In situ fabrication and microstructure of Al2O3 particles reinforced aluminum matrix composites

Effect of Precipitation Heat Treatment on a Mechanically Alloyed Al‐Based Composite Reinforced with Metallic Glassy Powder

Aging behavior and tensile properties of 6061Al–0.3 μm Al2O3p particle composites produced by reciprocating extrusion

Effectively enhanced strength by interfacial reactions in in-situ carbon reinforced Al matrix composites

Rare-Earth Oxide Coating for Sub-Micro Particulates Reinforced Aluminum Matrix Composites

Enhanced mechanical properties of a novel heat resistant Al-based composite reinforced by the combination of nano-aluminides and submicron TiN particles

Increasing the ductility of heat-resistant AlNp/Al composites by submicron Al2O3 particles

Enhanced Combination of Strength and Ductility in Ultrafine-Grained Aluminum Composites Reinforced with High Content Intragranular Nanoparticles