Abstract:A reciprocating extrusion process was developed to consolidate 6061-Al 2 O 3 p composites from mixed powders. The 6061 alloy powder was first dehydrated in a vacuum chamber at 450 °C and then mixed with 12.5 µm Al 2 O 3 powder in various volume fractions: 0, 5, 10, 20, and 30 pct. The mixed powders were hot pressed at 300 °C under a pressure of 300 MPa and finally extruded reciprocatingly 14 times at 460 °C. The results show that the composites were fully densified, with no sign of pores or oxide layers observable in the optical microscope. The Al 2 O 3 particles were distributed uniformly in the matrix. As compared with 6061 alloys, the composites demonstrated a smaller precipitation hardening and elongation, but exhibited a higher Young’s modulus and a larger work hardening capacity. The degradation of precipitation hardening was due to the loss of Mg, which reacts with Al 2 O 3 to form MgAl 2 O 4 . The large work-hardening capacity is attributable to the incompatibility between Al 2 O 3 and the matrix, which possibly generates more dislocations to harden the matrix. The composites had much higher friction coefficients and greater wear resistances than the 6061 alloy against steel disc surface. The friction coefficient of the 6061-30 vol pct Al 2 O 3 p composite was double that of the 6061 alloy and the wear resistance was 100-fold. As compared with similar composites reported previously, these composites possessed much higher elongation at the same strength level. A 30 vol pct Al 2 O 3 p still displayed an elongation of 9.8 pct in the T6 condition. All of these improvements are attributed to the merits, including full densification of the bulk, uniform dispersion of the Al 2 O 3 particles in the matrix, and strong binding between the Al 2 O 3 particles and the matrix resulting from reciprocating extrusion.

Aging behavior and tensile properties of 6061Al–0.3 μm Al2O3p particle composites produced by reciprocating extrusion

MMCs with Controlled Non-Uniform Distribution of Submicrometre Al2O3particles in 6061 Aluminium Alloy Matrix

Study of 6061-Al2o3p Composites Produced by Reciprocating Extrusion

MICROSTRUCTURES AND PROPERTIES OF HOT-EXTRUDED SiCW/6061Al COMPOSITES

High Strength Al–Al2O3p Composites: Optimization of Extrusion Parameters

High Strength Al(2)O(3)P/6061 Al Composites: Effect Of Particles, Subgrains And Precipitates

High strength Al<SUB>2</SUB>O<SUB>3p</SUB>/6061 Al composites: effect of particles, subgrains and precipitates

An in Situ Composite of Al (graphite, Al4C3) Produced by Reciprocating Extrusion

Rare-earth modification of sub-micron Al2O3 particle surface and its effect on the aging behavior of 6061Al composite

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF Y2O3 MODIFIED-Al2O3 PARTICLE /6061Al COMPOSITES

Artificial age hardening behavior of a squeeze cast CoCrFeMnNi high entropy alloy reinforced 6082-aluminium matrix composite

Strengthening mechanism and anisotropy of mechanical properties of Si3N4p/Al-Mg-Si composites fabricated by sintering and extrusion

In situ processing and aging behaviour of an aluminium/Al2O3 composite

Aging and Thermal Expansion Behavior of Si3N4p/2024Al Composite Fabricated by Pressure Infiltration Method

Effect of Aging Treatment on the Mechanical Properties of 45 vol.% SiCp/6061Al Composite

Effect of Aging Treatment on Microstructure and Mechanical Properties of As-Extruded AA6063 Aluminum Alloy

Effect of the interfacial reaction of aluminum and yttrium oxide on aging behavior of aluminum–magnesium–silicon alloy reinforced with yttrium oxide modified sub-micron alumina

Effect of surface modification of Al2O3 powder with Y2O3 on microstructure and tensile properties of aluninium matrix composites

Synergistic effects of cold rolling and age hardening on the hardness and tensile characteristics of AA6061 hybrid composites

Microstructures, mechanical properties, and aging behavior of hybrid-sized TiB2 particulate-reinforced 2219 aluminum matrix composites

Hot compression behaviors and microstructural evolution of Be-38wt.%6061Al