Rare-earth modification of sub-micron Al2O3 particle surface and its effect on the aging behavior of 6061Al composite

GH Wu,ZQ Yu,DL Sun,LT Jiang

DOI: https://doi.org/10.3321/j.issn:0412-1961.2003.08.018

IF: 1.797

2003-01-01

ACTA METALLURGICA SINICA

Abstract:Liquid coated approach was used in rare-earth modification on the surface of submicron Al2O3 particles, and a 6061 Al matrix composite reinforced by the modified Al2O3 particles was fabricated using squeeze-casting technique. The aging precipitation behaviors of sub-micron Al2O3p/6061Al composites before and after modification of Al2O3 particles at different aging temperatures were analysed. The results indicate that the modified sub-micron Al2O3 particle surfaces are coated homogeneously and the hardness of the modified-Al2O3p/6061Al composite is obviously increased comparing to the as-received Al2O3p/6061Al at different aging states. With increasing of temperature the precipitation processes (Mg2Si) become accelerated, the time to reach the peak hardness is shortened and the hardness peak value is reduced. TEM observation of the aging microstructure shows that some dislocations and precipitates exist in Al-matrix of modified-Al2O3p/6061Al composite, but only rare dislocation and precipitates exist in as-received Al2O3p/6061Al. The reasons of the above aging microstructure difference are discussed.