Microstructure study of hot rolling nanosized in-situ Al2O3 particle reinforced A356 matrix composites

Guirong Li,Tuo Xu,Hongming Wang,Yutao Zhao,Gang Chen,Xizhou Kai

DOI: https://doi.org/10.1016/j.jallcom.2020.157107

IF: 6.2

2021-02-01

Journal of Alloys and Compounds

Abstract:<p>In this study, A356 matrix and 0.2 vol%∼0.8 vol% in-situ Al₂O_3p/A356 composite were hot rolled to 75% reduction ratio and 0.6 vol% composite was hot rolled to 75% and 83% reduction ratios. Scanning electron microscope (SEM), Electron back scattering diffraction (EBSD) and transmission electron microscopy (TEM) were used to characterize the microstructure and texture evolution so as to investigate the effect of the particle content and reduction ratios. In the 75% rolling reduction, the Si phase in the A356 matrix and Al₂O_3p/A356 composites was fragmented and distributed along the rolling direction (RD), obvious Al₂O₃ agglomeration diminished. On the state of 75% reduction, when the content of Al₂O₃ was 0.2 vol%, the composite had the finest grain size, however the 0.6 vol% composite had a better Si phase and Al₂O₃ distribution. The Al₂O₃ particle in 0.2 vol% sample can enhance the dislocation density and accelerate the sub-grain boundary formation. For the 75% reduction materials, the tensile properties increased with increase of particulate content to 0.6 vol% then decreased. The mechanical properties of 83% rolling reduction sample was better than the 75% reduction. Tensile tests showed that the ultimate tensile strength (UTS), yield strength (YS) and elongation (El) of 0.6 vol% Al₂O_3p/A356 composite increased to 282 MPa, 221 MPa and 17.5%, respectively, due to the uniform distribution of the particles and refined Si phase upon increasing the rolling reduction to 83%, in combination with T4 heat treatment. In addition, the mechanisms of particle dispersion, recrystallization grain refinement and strengthening are also discussed.</p>

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problems that this paper attempts to solve are mainly to introduce in - situ generated nano - Al_2O_3 particles with different volume fractions into A356 aluminum alloy and conduct hot - rolling treatment, so as to improve the microstructure and mechanical properties of the material. Specifically, the research focuses on the following aspects:

1. **Improvement of microstructure**: By adding different contents of Al_2O_3 particles and conducting hot - rolling treatment with different reduction ratios, the influence of particle content and reduction ratio on the microstructure of A356 matrix and composites is studied. In particular, the morphological change of Si phase, the distribution of Al_2O_3 particles and the effect of grain refinement are observed.

2. **Enhancement of mechanical properties**: The tensile properties of composites treated under different conditions are evaluated, including ultimate tensile strength (UTS), yield strength (YS) and elongation (El), and the variation rules of these properties with particle content and reduction ratio are explored.

3. **Mechanism analysis**: The particle dispersion, recrystallization grain refinement and strengthening mechanisms are explored to explain why the mechanical properties of the material are significantly improved under certain conditions.

Through these studies, the paper aims to find an effective method to improve the strength and plasticity of A356 aluminum alloy, making it more suitable for industrial applications.