In situ formation mechanism of aluminum oxycarbonitride in the unoxidized zone of Al–Al2O3 composites
Mengyao Yang,Guoqing Xiao,Donghai Ding,Yifan Yang,Mingxue Jiang,Dingao Yang,Shouqian Yuan
DOI: https://doi.org/10.1016/j.ceramint.2021.05.008
IF: 5.532
2021-08-01
Ceramics International
Abstract:The Al–Al2O3 composites were prepared by fused alumina, α-Al2O3 micropowders, and metal aluminum powder. The samples with 3% carbon black (N330), 3% resin powder and α-Al2O3 micropowder, 10% α-Al2O3 micropowder were named S1, S2, and S3, respectively. They were oxidized at 1500 °C for 3 h in a box-type electric furnace, and then the unoxidized areas were analyzed by X-ray diffraction and scanning electron microscopy. It was found that the aluminum oxycarbonitride formed in situ during the oxidation resistance test inhibited further oxidation of S2. The in situ formation mechanism of aluminum oxycarbonitride in the unoxidized zone is believed to be 7Al + 3Al3C4 + 12AlN + 4Al2O3 = 12Al3CON, which is also verified and proven by XRD, SEM and EDS in this work. The oxidation depth of S2 is 46.7% lower than that of S3. Sample S2 hardly has any linear change after fired at 1500 °C × 3 h in coke, which benefits to improve the volume stability and prolongs the service life. Among the three batches, S2 exhibits the minimum creep rate, from 0% to 0.026% at 1500 °C, and the HMOR at 1500 °C in a N2 atmosphere of S2 is 58 MPa. The Al–Al2O3 composites combined with resin strengthened by in situ formed aluminum oxycarbonitride give the composites excellent high-temperature strength owing to the fiber-intersected reinforced microstructure of Al3CON crystals at high temperature. In the Al–C–N–O system, it was found that the general formula of aluminum oxycarbonitride is expressed by Al4n+m(C,O,N)3n+m, and the (n, m) values are (0, 3) for Al3CON.
materials science, ceramics