Abstract:With high activity h-BN powders as raw materials and without the using of any sintering additives, AlN–BN composite ceramics with 0–30 vol% were prepared by hot-pressing sintering in N2 at 1850 °C. Effect of h-BN content on the microstructure and properties of the composite ceramics was investigated. The results show that fully dense composite ceramics with h-BN content up to 20 vol% can be obtained and all composites show a fine-grain-microstructure with clean and clear boundaries. No “card room structure” of h-BN was formed in the samples. With the increasing h-BN content, the composites show a decreased bending strength, fracture toughness, Vickers hardness, thermal conductivity and dielectric constant. The application of high activity raw materials produces a significant grain-refinement strengthening effect and makes the composites exhibit a much higher strength and toughness compared with the results reported by other researchers. Due to the absence of sintering additive, the composite ceramics also show a quite low dielectric loss at both low and high frequency. An optimal comprehensive properties are obtained for the AlN-20 vol% BN composite: bending strength of 410 ± 21 MPa, fracture toughness of 4.21 ± 0.19 MPa·m1/2, Vickers hardness of 7.7 ± 0.2 GPa, thermal conductivity of 46.6 W·m−1·K−1, dielectric constant of 7.4 (1 MHz) and 7.48 (18 GHz), dielectric loss of 6.7 × 10−4 (1 MHz) and 6.18 × 10−3 (18 GHz).

Dielectric Properties of Boron Nitride-Aluminium Nitride Composites Prepared by Spark Plasma Sintering

High pressure sintering behavior and mechanical properties of cBN-Ti 3Al and cBN-Ti 3Al-Al composite materials

Improvement in mechanical properties in AlN-h-BN composites with high thermal conductivity

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Preparation and properties of sintering additive-free AlN–BN composite ceramics by hot-pressing sintering

Dielectric properties of AlB-BN composite ceramics

Fabrication and thermal conductivity of AlN/BN ceramics by spark plasma sintering

Boron Nitride?Aluminum Nitride Ceramic Composites Fabricated by Transient Plastic Phase Processing

High-pressure synthesis of Al<sub>2</sub>O<sub>3</sub>-cBN composites: Effect of thermodynamic condition and cBN volume fraction on their microstructure and properties

Fabrication and properties of porous boron nitride/silicon oxynitride ceramic composites via gas pressure sintering

Preparation and Properties of BNw/Si3N4 Wave-Transparent Composites by Spark Plasma Sintering

Spark plasma sintering of TiN–TiB2–hBN composites and their properties

Preparation and properties of porous Si 3N 4/SiO 2/BN composite ceramics

Preparation and Properties of Porous Si<sub>3</sub>N<sub>4</sub>/SiO<sub>2</sub>/BN Composite Ceramics

Dielectric and Mechanical Properties of Porous Si3N4-BN Ceramic Composites

Thermal conductivity and dielectric property of hot-pressing sintered AlN–BN ceramic composites

Modulation of dielectric properties of hexagonal/cubic boron nitride composites

Flexural strength, thermal and dielectric properties of AlN ceramics with BN nanoplatelets addition

Effect of Boron Nitride Addition on Densification, Microstructure, Mechanical, Thermal, and Dielectric Properties of β-SiAlON Ceramic

Reaction-Bonded Boron Nitride-Aluminum Nitride Ceramic Composites

Mechanical, dielectric and thermal properties of porous boron nitride/silicon oxynitride ceramic composites prepared by pressureless sintering