Mechanical, dielectric and thermal properties of porous boron nitride/silicon oxynitride ceramic composites prepared by pressureless sintering

Yangshan Sun,Zhihua Yang,Delong Cai,Qian Li,Hailiang Li,Shengjin Wang,Dechang Jia,Yu Zhou

DOI: https://doi.org/10.1016/j.ceramint.2017.03.151

IF: 5.532

2017-08-01

Ceramics International

Abstract:Porous boron nitride/silicon oxynitride (BN/Si2N2O) composites were fabricated by pressureless sintering at 1650°C with Li2O as sintering aid. The influence of Li2O and hexagonal boron nitride (h-BN) contents on phase, microstructure, mechanical, dielectric and thermal properties of the resulting porous BN/Si2N2O composites was investigated. Increasing Li2O content facilitated densification and decomposition of Si2N2O into Si3N4. The apparent porosity of the composites increases with the h-BN content increases and Si2N2O grain growth was restrained by the dispersed h-BN particles. The dielectric properties and thermal conductivities (TC) were affected mainly by porosity. Porous BN/Si2N2O ceramic composites with 4mol% Li2O and 25mol% BN exhibit both low dielectric constant (3.83) and dielectric loss tangent (0.008) with good mechanical and thermal performance, suggesting possible use as high-temperature structural/functional materials.

materials science, ceramics