Abstract:A series of Si-rich amorphous silicon carbide (a-SiC:H) thin films were deposited in conventional plasma enhanced chemical vapor deposition system with various gas ratio R = [CH 4 ]/[SiH 4 ]. The microstructural, optical and electronic properties of as-deposited films were investigated in this study. It was found that optical band gap was linearly proportional to carbon content in the films and it could be controlled in a range of 1.8–2.4 eV by changing the gas ratio, R . Both dark and photo conductivities in room temperature were decreased with the increasing of carbon content in the films, and the photosensitivity reached as high as 10 4 for the film with the optical band gap of 1.96 eV. The as-deposited samples were subsequently annealed at the temperatures of 900°C and 1000°C. The formation of nanocrystalline silicon (nc-Si) dots in amorphous silicon carbide (a-SiC) host matrix was shown. The dark conductivity was enhanced by five orders of magnitude after annealing compared with that of as-deposited films. The result of temperature-dependent conductivity suggested that the property of carrier transport was dominated by conduction process between the extended states. Furthermore, room temperature electroluminescence (EL) was achieved from nc-Si/SiC system and the possible mechanism of radiative recombination mechanism was discussed.

Annealing Environment Effect on the Nanocrystalline Silicon Related Photoluminescence in Silicon Rich Alumina Films

Influence of annealing on microstructures and photoluminescence of nano-composite silicon film

Effect of annealing on microstructure and photoluminescence of nano-composite silicon film

Nanocrystal and Interface Defects Related Photoluminescence in Silicon-Rich Al2O3 Films

Effect of Post-Annealing in Oxygen Atmosphere on the Photoluminescence Properties of Nc-Si Rich Sio2 Films

Effect of Annealing Temperature on Photoluminescence Performance and Structure of Si-rich Silicon Nitride

Optical Properties of Nanocrystal-Silicon Thin Films on Silicon Nanopillar Arrays after Thermal Annealing

Preparation and Photoluminescence of Nanocrystalline Si-Rich Silicon Oxide Films by Pecvd

Photoluminescence Enhancement of Si Nanocrystals Embedded in SiO 2 by Thermal Annealing in Air

Sensitizing Properties of Luminescence Centers on the Emission of Er3+ in Si-Rich Sio2 Film

Annealing Effect on Optical and Electronic Properties of Silicon Rich Amorphous Silicon-Carbide Films

Annealing effect on structures and luminescence of amorphous SiN films

Optical Properties of High Photoluminescence Silicon Nanocrystals Embedded in SiO2 Matrices Obtained by Annealing Hydrogen Silsesquioxane

Effects of Excess Silicon on the 1540 Nm Er3+ Luminescence in Silicon Rich Oxynitride Films

Efficient Sensitized Photoluminescence of Er Silicate in Silicon Oxide Films Embedded with Amorphous Silicon Clusters, Part I: Fabrication

Study on Phase Separation in A-Siox for Si Nanocrystal Formation Through the Correlation of Photoluminescence with Structural and Optical Properties

Enhanced Electroluminescence of Silicon-Rich Silicon Nitride Light-Emitting Devices by Nh3 Plasma and Annealing Treatment

Sensitization of Er3+ Ions in Silicon Rich Oxynitride Films: Effect of Thermal Treatments

Pseudo Nanocrystal Silicon Induced Luminescence Enhancement in A-Si /sio 2 Multilayers

Pseudo nanocrystal silicon induced luminescence enhancement in a-Si /SiO2 multilayers

High Temperature Annealing Behaviors of Luminescent SIOx : H Films